DSM Stanyl® TW242FM10 PA46-(GF+MF)50

Category	Polymer , Thermoplastic , Nylon , Nylon 46 , Nylon 46, Glass Fiber Reinforced
Manufacturer	DSM Engineering Plastics
Trade Name	Stanyl®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DSM Stanyl® TW242FM10 PA46-(GF+MF)50.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

50% Glass/Mineral Reinforced, Heat Stabilized

Physical Properties	Metric	English	Comments
Density	1.63 g/cc	0.0589 lb/in³	dry; ISO 1183
Moisture Absorption	1.80 %	1.80 %	Sim. To ISO 62
Linear Mold Shrinkage, Flow	0.0020 cm/cm	0.0020 in/in	Sim. To ISO 294-4
Linear Mold Shrinkage, Transverse	0.0125 cm/cm	0.0125 in/in	Sim. To ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	160 MPa	23200 psi	dry; ISO 527-1/-2
Elongation at Break	2.0 %	2.0 %	dry; ISO 527-1/-2
Tensile Modulus	14.5 GPa	2100 ksi	dry; ISO 527-1/-2
Flexural Modulus	11.0 GPa	1600 ksi	dry; ISO 178
Izod Impact Resistance	0.400 J/cm² @Temperature -40.0 °C	1.90 ft-lb/in² @Temperature -40.0 °F	dry; ISO 180/1A
	0.600 J/cm² @Temperature 23.0 °C	2.86 ft-lb/in² @Temperature 73.4 °F	dry; ISO 180/1A
Charpy Impact, Notched	0.450 J/cm² @Temperature -30.0 °C	2.14 ft-lb/in² @Temperature -22.0 °F	dry; ISO 179/1eA
	0.600 J/cm² @Temperature 23.0 °C	2.86 ft-lb/in² @Temperature 73.4 °F	dry; ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	25.0 µm/m-°C	13.9 µin/in-°F	dry; ISO 11359-1/-2
CTE, linear, Transverse to Flow	50.0 µm/m-°C	27.8 µin/in-°F	dry; ISO 11359-1/-2
Melting Point	295 °C	563 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi)	285 °C	545 °F	dry; ISO 75-1/-2