DSM Stanyl® TS200F10 PA46-GF50

Category Polymer , Thermoplastic , Nylon , Nylon 46 , Nylon 46, Glass Fiber Reinforced
Manufacturer DSM Engineering Plastics
Trade Name Stanyl®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DSM Stanyl® TS200F10 PA46-GF50.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
50% Glass Reinforced
Physical Properties Metric English Comments
Density 1.62 g/cc
0.0585 lb/in³
dry; ISO 1183
Moisture Absorption 1.85 %
1.85 %
Sim. To ISO 62
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
Sim. To ISO 294-4
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
0.0090 in/in
Sim. To ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 160 MPa
23200 psi
cond; ISO 527-1/-2
250 MPa
36300 psi
dry; ISO 527-1/-2
100 MPa

@Temperature 200 °C
 14500 psi

@Temperature 392 °F
 ISO 527-1/-2
110 MPa

@Temperature 180 °C
 16000 psi

@Temperature 356 °F
 ISO 527-1/-2
120 MPa

@Temperature 160 °C
 17400 psi

@Temperature 320 °F
 ISO 527-1/-2
140 MPa

@Temperature 120 °C
 20300 psi

@Temperature 248 °F
 ISO 527-1/-2
Elongation at Break 2.7 %
2.7 %
dry; ISO 527-1/-2
5.0 %
5.0 %
cond; ISO 527-1/-2
5.0 %

@Temperature 120 °C
 5.0 %

@Temperature 248 °F
 ISO 527-1/-2
5.0 %

@Temperature 160 °C
 5.0 %

@Temperature 320 °F
 ISO 527-1/-2
5.0 %

@Temperature 180 °C
 5.0 %

@Temperature 356 °F
 ISO 527-1/-2
5.0 %

@Temperature 200 °C
 5.0 %

@Temperature 392 °F
 ISO 527-1/-2
Tensile Modulus 10.0 GPa
1450 ksi
cond; ISO 527-1/-2
16.0 GPa
2320 ksi
dry; ISO 527-1/-2
6.60 GPa

@Temperature 200 °C
 957 ksi

@Temperature 392 °F
 ISO 527-1/-2
7.00 GPa

@Temperature 180 °C
 1020 ksi

@Temperature 356 °F
 ISO 527-1/-2
7.40 GPa

@Temperature 160 °C
 1070 ksi

@Temperature 320 °F
 ISO 527-1/-2
8.20 GPa

@Temperature 120 °C
 1190 ksi

@Temperature 248 °F
 ISO 527-1/-2
Flexural Modulus 9.00 GPa
1310 ksi
cond; ISO 178
14.0 GPa
2030 ksi
dry; ISO 178
6.50 GPa

@Temperature 160 °C
 943 ksi

@Temperature 320 °F
 ISO 178
7.30 GPa

@Temperature 120 °C
 1060 ksi

@Temperature 248 °F
 ISO 178
Izod Impact Resistance 1.40 J/cm²

@Temperature -40.0 °C
 6.66 ft-lb/in²

@Temperature -40.0 °F
 cond; ISO 180/1A
1.40 J/cm²

@Temperature -40.0 °C
 6.66 ft-lb/in²

@Temperature -40.0 °F
 dry; ISO 180/1A
1.60 J/cm²

@Temperature 23.0 °C
 7.61 ft-lb/in²

@Temperature 73.4 °F
 dry; ISO 180/1A
2.40 J/cm²

@Temperature 23.0 °C
 11.4 ft-lb/in²

@Temperature 73.4 °F
 cond; ISO 180/1A
Charpy Impact Unnotched 9.00 J/cm²

@Temperature -30.0 °C
 42.8 ft-lb/in²

@Temperature -22.0 °F
 dry; ISO 179/1eU
10.0 J/cm²

@Temperature 23.0 °C
 47.6 ft-lb/in²

@Temperature 73.4 °F
 dry; ISO 179/1eU
10.0 J/cm²

@Temperature -30.0 °C
 47.6 ft-lb/in²

@Temperature -22.0 °F
 cond; ISO 179/1eU
11.0 J/cm²

@Temperature 23.0 °C
 52.3 ft-lb/in²

@Temperature 73.4 °F
 cond; ISO 179/1eU
Charpy Impact, Notched 1.40 J/cm²

@Temperature -30.0 °C
 6.66 ft-lb/in²

@Temperature -22.0 °F
 cond; ISO 179/1eA
1.40 J/cm²

@Temperature -30.0 °C
 6.66 ft-lb/in²

@Temperature -22.0 °F
 dry; ISO 179/1eA
1.60 J/cm²

@Temperature 23.0 °C
 7.61 ft-lb/in²

@Temperature 73.4 °F
 dry; ISO 179/1eA
2.40 J/cm²

@Temperature 23.0 °C
 11.4 ft-lb/in²

@Temperature 73.4 °F
 cond; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.0 µm/m-°C
13.9 µin/in-°F
dry; ISO 11359-1/-2
CTE, linear, Transverse to Flow 40.0 µm/m-°C
22.2 µin/in-°F
dry; ISO 11359-1/-2
Melting Point 295 °C
563 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi) 290 °C
554 °F
dry; ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 dry; IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+10 ohm-cm
1.00e+10 ohm-cm
cond; IEC 60093
1.00e+14 ohm-cm
1.00e+14 ohm-cm
dry; IEC 60093
Dielectric Strength 20.0 kV/mm
508 kV/in
cond; IEC 60243-1
30.0 kV/mm
762 kV/in
dry; IEC 60243-1
Comparative Tracking Index 300 V
300 V
dry; IEC 60112