DSM Stanyl® OCD2300 BLK PA46-GF50

Category Polymer , Thermoplastic , Nylon , Nylon 46 , Nylon 46, Glass Fiber Reinforced
Manufacturer DSM Engineering Plastics
Trade Name Stanyl®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DSM Stanyl® OCD2300 BLK PA46-GF50.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
50% Glass Reinforced, Heat Stabilized
Physical Properties Metric English Comments
Density 1.62 g/cc
0.0585 lb/in³
dry; ISO 1183
Moisture Absorption 2.20 %
2.20 %
Sim. To ISO 62
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 135 MPa
19600 psi
cond; ISO 527-1/-2
240 MPa
34800 psi
dry; ISO 527-1/-2
60.0 MPa

@Temperature 200 °C
8700 psi

@Temperature 392 °F
ISO 527-1/-2
75.0 MPa

@Temperature 180 °C
10900 psi

@Temperature 356 °F
ISO 527-1/-2
90.0 MPa

@Temperature 160 °C
13100 psi

@Temperature 320 °F
ISO 527-1/-2
110 MPa

@Temperature 120 °C
16000 psi

@Temperature 248 °F
ISO 527-1/-2
Elongation at Break 2.4 %
2.4 %
dry; ISO 527-1/-2
6.3 %
6.3 %
cond; ISO 527-1/-2
7.5 %

@Temperature 120 °C
7.5 %

@Temperature 248 °F
ISO 527-1/-2
8.5 %

@Temperature 160 °C
8.5 %

@Temperature 320 °F
ISO 527-1/-2
9.0 %

@Temperature 180 °C
9.0 %

@Temperature 356 °F
ISO 527-1/-2
9.5 %

@Temperature 200 °C
9.5 %

@Temperature 392 °F
ISO 527-1/-2
Tensile Modulus 8.00 GPa
1160 ksi
cond; ISO 527-1/-2
17.0 GPa
2470 ksi
dry; ISO 527-1/-2
4.50 GPa

@Temperature 200 °C
653 ksi

@Temperature 392 °F
ISO 527-1/-2
5.60 GPa

@Temperature 180 °C
812 ksi

@Temperature 356 °F
ISO 527-1/-2
6.10 GPa

@Temperature 160 °C
885 ksi

@Temperature 320 °F
ISO 527-1/-2
6.90 GPa

@Temperature 120 °C
1000 ksi

@Temperature 248 °F
ISO 527-1/-2
Flexural Modulus 8.00 GPa
1160 ksi
cond; ISO 178
17.0 GPa
2470 ksi
dry; ISO 178
4.50 GPa

@Temperature 200 °C
653 ksi

@Temperature 392 °F
ISO 178
5.60 GPa

@Temperature 180 °C
812 ksi

@Temperature 356 °F
ISO 178
6.10 GPa

@Temperature 160 °C
885 ksi

@Temperature 320 °F
ISO 178
6.90 GPa

@Temperature 120 °C
1000 ksi

@Temperature 248 °F
ISO 178
Charpy Impact Unnotched 8.00 J/cm²

@Temperature -30.0 °C
38.1 ft-lb/in²

@Temperature -22.0 °F
dry; ISO 179/1eU
9.50 J/cm²

@Temperature 23.0 °C
45.2 ft-lb/in²

@Temperature 73.4 °F
dry; ISO 179/1eU
9.50 J/cm²

@Temperature -30.0 °C
45.2 ft-lb/in²

@Temperature -22.0 °F
cond; ISO 179/1eU
11.0 J/cm²

@Temperature 23.0 °C
52.3 ft-lb/in²

@Temperature 73.4 °F
cond; ISO 179/1eU
Charpy Impact, Notched 1.40 J/cm²

@Temperature -30.0 °C
6.66 ft-lb/in²

@Temperature -22.0 °F
cond; ISO 179/1eA
1.40 J/cm²

@Temperature -30.0 °C
6.66 ft-lb/in²

@Temperature -22.0 °F
dry; ISO 179/1eA
1.70 J/cm²

@Temperature 23.0 °C
8.09 ft-lb/in²

@Temperature 73.4 °F
dry; ISO 179/1eA
3.00 J/cm²

@Temperature 23.0 °C
14.3 ft-lb/in²

@Temperature 73.4 °F
cond; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.0 µm/m-°C
13.9 µin/in-°F
dry; ISO 11359-1/-2
CTE, linear, Transverse to Flow 40.0 µm/m-°C
22.2 µin/in-°F
dry; ISO 11359-1/-2
Melting Point 282 °C
540 °F
10°C/min; ISO 11357-1/-3