DSM Novamid® 1010N2 1ES NAT PA6 FR(30)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Novamid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Novamid® 1010N2 1ES NAT PA6 FR(30).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection Molding, Flame Retardant (Halogen free)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 3.00 % | 3.00 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm | 0.010 in/in | Sim. To ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | Sim. To ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | cond; ISO 527-1/-2 |
| 80.0 MPa | 11600 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 5.0 % | 5.0 % | dry; ISO 527-1/-2 |
| >= 50 % | >= 50 % | cond; ISO 527-1/-2 | |
| Elongation at Yield | 4.8 % | 4.8 % | dry; ISO 527-1/-2 |
| 22 % | 22 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 1.50 GPa | 218 ksi | cond; ISO 527-1/-2 |
| 3.60 GPa | 522 ksi | dry; ISO 527-1/-2 | |
| Flexural Strength | 46.0 MPa | 6670 psi | cond; ISO 178 |
| 120 MPa | 17400 psi | dry; ISO 178 | |
| Flexural Modulus | 1.40 GPa | 203 ksi | cond; ISO 178 |
| 3.60 GPa | 522 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | 9.00 J/cm² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 0.300 J/cm² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA |
| 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 60.0 µm/m-°C | 33.3 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | dry; ISO 11359-1/-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 192 °C | 378 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
dry; IEC 60695-11-10 |
| Glow Wire Test | 960 °C @Thickness 3.00 mm |
1760 °F @Thickness 0.118 in |
Glow Wire Flammability Index, dry; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | dry; IEC 60093 |
| Surface Resistance | 2.00e+14 ohm | 2.00e+14 ohm | cond; IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
dry; IEC 60250 |
| 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
dry; IEC 60250 | |
| Dielectric Strength | 26.0 kV/mm | 660 kV/in | dry; IEC 60243-1 |
| Dissipation Factor | 0.010 @Frequency 100 Hz |
0.010 @Frequency 100 Hz |
dry; IEC 60250 |
| 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
dry; IEC 60250 | |
| Comparative Tracking Index | 550 V | 550 V | dry; IEC 60112 |