DSM Arnitel® UM622 Polyether Ester Elastomer (European Grade)  (discontinued **)

Category Polymer , Thermoplastic , Elastomer, TPE , Polyester TPE , Polyester, TP , Polyether Ester Elastomer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DSM Arnitel® UM622 Polyether Ester Elastomer (European Grade)  (discontinued **).pdf
  Online Service   lookpolymers   27660005
Material Notes:
Product description: Arnitel® combines the advantages of engineering thermoplastics, being easy to process with excellent mechanical properties, at the same time with the flexibility of rubbers.Arnitel does not require vulcanization. This leads to substantial reductions in part cost. Arnitel can be used over a wide range of temperatures. Arnitel has exceptional fatigue, creep resistance and resistance to oils, greases and many other chemicals.Characteristics of Arnitel:Excellent strength over a wide range of temperaturesExcellent dynamic properties e.g. creep and fatigueHigh heat resistanceExceptional resistance to oils and greasesGood chemical resistanceHigh degree of versatility in processingEasy coloring using masterbatchesSurface quality from high gloss to texturedExcellent heat resistance (long term 165°C)Good electrical insulation propertiesLow moisture absorption, excellent dimensional stabilityEasy flow, fast cooling timesTypical Applications: Automotive: Arnitel® is extensively used in the automotive industry for applications requiring exceptional fatigue resistance and resistance to oil and greases. Examples are: Rack and Pinion Bellows, Constant Velocity Joint Boots (CVJ Boots), Air brake tubings.Arnitel in the Electronic and Consumer Goods Industry: Arnitel® finds enormous potential and is also widely used in the consumer electronics by some of the world's best companies. Arnitel® is the best choice for low noise gears where their exceptional processability without any defects such as flash, makes it the material solution of choice. Arnitel® is also used in highly demanding applications such as in mobile phone antennas.Arnitel® has exceptional flexibility and can perform or even outperform functions that normally require conventional rubbers. Available in a wide range of hardnesses, Arnitel can replace metals, thermoplastics, leather and rubber, often with a reduction in finished part costs.Information provided by DSM.
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
ISO 1183
Water Absorption 0.60 %
0.60 %
Sim. to ISO 62
Moisture Absorption at Equilibrium 0.25 %
0.25 %
Humidity Absorption; Sim. to ISO 62
Melt Flow 38.1 g/10 min

@Load 2.16 kg,
Temperature 240 °C
38.1 g/10 min

@Load 4.76 lb,
Temperature 464 °F
Calculated from Volume Flow Rate of 30 cm<sup>3</sup>/10min.; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 62
3s; ISO 868
Tensile Strength at Break 30.0 MPa
4350 psi
ISO 527-1/-2
Tensile Strength, Yield 14.0 MPa

@Strain 5.00 %
2030 psi

@Strain 5.00 %
ISO 527-1/-2
19.0 MPa

@Strain 10.0 %
2760 psi

@Strain 10.0 %
ISO 527-1/-2
21.0 MPa

@Strain 50.0 %
3050 psi

@Strain 50.0 %
ISO 527-1/-2
Elongation at Break 325 %
325 %
ISO 527-1/-2
Tensile Modulus 0.350 GPa
50.8 ksi
ISO 527-1/-2
Izod Impact, Notched (ISO) NB

@Temperature 23.0 °C

@Temperature 73.4 °F
ISO 180/1A
Charpy Impact, Notched 0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA

@Temperature 23.0 °C

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 160 µm/m-°C

@Temperature 20.0 °C
88.9 µin/in-°F

@Temperature 68.0 °F
ISO 11359-1/-2
Melting Point 220 °C
428 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 80.0 °C
176 °F
ISO 75-1/-2
Vicat Softening Point 85.0 °C
185 °F
50°C/h 50N; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm

@Thickness 0.0630 in
IEC 60695-11-10

@Thickness 0.750 mm

@Thickness 0.0295 in
IEC 60695-11-10
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
IEC 60112
Descriptive Properties Value Comments
Coating Yes
Film Extrusion Yes
Heat stabilized or stable to heat Yes
High impact or impact modified Yes
Injection molding Yes
Light stabilized or stable to light Yes
Other Extrusion Yes
Sheet extrusion Yes
U.V. stabilized or stable to weather Yes
Without Fillers Yes