DSM Akulon® K222-KMV5 /A PA6-MD25 FR(30)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Mineral Filled |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Akulon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Akulon® K222-KMV5 /A PA6-MD25 FR(30).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
25% Mineral Reinforced, Flame Retardant (Halogen free), Color Stabilized
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | dry; ISO 1183 |
| Water Absorption | 6.2 % | 6.2 % | Sim. To ISO 62 |
| Moisture Absorption | 1.80 % | 1.80 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0091 cm/cm | 0.0091 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0082 cm/cm | 0.0082 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | cond; ISO 527-1/-2 |
| 65.0 MPa | 9430 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 2.5 % | 2.5 % | dry; ISO 527-1/-2 |
| 30 % | 30 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 2.50 GPa | 363 ksi | cond; ISO 527-1/-2 |
| 6.00 GPa | 870 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | 2.50 J/cm² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eU |
| 2.90 J/cm² @Temperature 23.0 °C |
13.8 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU | |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature 23.0 °C |
0.952 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA |
| 0.200 J/cm² @Temperature -30.0 °C |
0.952 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C | 27.8 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C | 27.8 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | V-2 @Thickness 1.50 mm |
V-2 @Thickness 0.0591 in |
dry; IEC 60695-11-10 |
| V-2 @Thickness 0.750 mm |
V-2 @Thickness 0.0295 in |
dry; IEC 60695-11-10 | |
| Glow Wire Test | 700 °C @Thickness 0.750 mm |
1290 °F @Thickness 0.0295 in |
Glow Wire Ignition Temperature, dry; IEC 60695-2-13 |
| 725 °C @Thickness 3.00 mm |
1340 °F @Thickness 0.118 in |
Glow Wire Ignition Temperature, dry; IEC 60695-2-13 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | dry; IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | cond; IEC 60093 |
| Comparative Tracking Index | 600 V | 600 V | cond; IEC 60112 |
Users viewing this material also viewed the following:
- NOVA Chemicals Sclair® 56B4 HDPE Blow Molding Resin
- SABIC Innovative Plastics LNP FARADEX NX07344 PC+ABS (Asia Pacific)
- Omnia Plastica Akulon® PET Arnite Omnialite
- Stir SpA C 2044 A AT (PVC)
- Entec Hyrene® PSCRY 8 General Purpose Polystyrene
- Dynasol Solprene® 200 Polybutadiene Rubber
- BASF Neopolen® P 9230 D 0.04 g/cc Core density; Expanded Polypropylene (Europe)
Copyright © lookpolymers.com All Rights Reserved