DSM Akulon® K-FHG12 (Dry) 60% Glass Reinforced Nylon 6 (North America)  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 60% Glass Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DSM Akulon® K-FHG12 (Dry) 60% Glass Reinforced Nylon 6 (North America)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt viscosities to suit all extrusion processes: barrier and coating film, tube and hose, monofilament, stock shapes. Akulon resins are characterized by:consistent qualityhigh purity for film applications, low gel contents. Molding ResinsSuited to all engineering demands: Unfilled low and medium viscosity gradesToughened unfilled gradesGlass reinforced from 20-45% filledLow warpage reinforced gradesFlame retardant; UL V0 rated and glow wire typesHalogen free FR gradesBlow moldable materialsLaser markable resinsLaser weldable, high burst pressure gradesToughened, reinforced resinsHigh stiffness grades for metal replacement Akulon Ultraflow resins have high flow with mechanical properties similar to standard materials. Exceptional flow allows: productivity gains in moldinglower built in stressesbetter surface appearancesystem cost reductions Applications for Molding resins There is an Akulon resin available suitable for any application requiring polyamides. Key areas where DSM has specific application knowledge areAutomotiveUnder the hood and engine componentsExterior and interior applicationsElectrical components and connectorsElectricalLow voltage power distributionLightingPower connectorsConsumer DurablesPower and lawn and garden toolsSmall AppliancesSports and leisure equipmentFurniture accessoriesIndustrial GoodsTransportation (railways)Information provided by DSM.
Physical Properties Metric English Comments
Density 1.66 g/cc
0.0600 lb/in³
ISO 1183
Water Absorption 3.6 %
3.6 %
Sim. to ISO 62
Moisture Absorption at Equilibrium 1.0 %
1.0 %
Humidity Absorption; Sim. to ISO 62
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 235 MPa
34100 psi
ISO 527-1/-2
Elongation at Break 2.2 %
2.2 %
ISO 527-1/-2
Tensile Modulus 20.0 GPa
2900 ksi
ISO 527-1/-2
Flexural Strength 360 MPa
52200 psi
ISO 178
Flexural Modulus 16.5 GPa
2390 ksi
ISO 178
Charpy Impact Unnotched 8.50 J/cm²

@Temperature -30.0 °C
40.5 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
9.00 J/cm²

@Temperature 23.0 °C
42.8 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 1.20 J/cm²

@Temperature -30.0 °C
5.71 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
1.50 J/cm²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 10.0 µm/m-°C

@Temperature 20.0 °C
5.56 µin/in-°F

@Temperature 68.0 °F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 40.0 µm/m-°C

@Temperature 20.0 °C
22.2 µin/in-°F

@Temperature 68.0 °F
ISO 11359-1/-2
Melting Point 220 °C
428 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
IEC 60695-11-10
Descriptive Properties Value Comments
Heat stabilized or stable to heat Yes
Injection molding Yes
With Fillers Yes