DSM Akulon® F130-C PA6

Category Polymer , Film , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Extruded
Manufacturer DSM Engineering Plastics
Trade Name Akulon®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DSM Akulon® F130-C PA6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Film Extrusion, Medium Viscosity, Lubricated
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Water Vapor Transmission 35.0 g/m²/day

@Temperature 23.0 °C
2.25 g/100 in²/day

@Temperature 73.4 °F
at 85% r.h., film; DIS 15106-1/-3
Oxygen Transmission 1.30 cc-mm/m²-24hr-atm

@Temperature 23.0 °C
3.30 cc-mil/100 in²-24hr-atm

@Temperature 73.4 °F
at 0% r.h., film; DIS 15105-1/-2
1.90 cc-mm/m²-24hr-atm

@Temperature 23.0 °C
4.83 cc-mil/100 in²-24hr-atm

@Temperature 73.4 °F
at 85% r.h., film; DIS 15105-1/-2
Viscosity 810000 cP

@Temperature 260 °C
810000 cP

@Temperature 500 °F
Melt Viscosity; DSM method
300000 cP

@Shear Rate 1000 1/s,
Temperature 280 °C
300000 cP

@Shear Rate 1000 1/s,
Temperature 536 °F
350000 cP

@Shear Rate 1000 1/s,
Temperature 260 °C
350000 cP

@Shear Rate 1000 1/s,
Temperature 500 °F
400000 cP

@Shear Rate 1000 1/s,
Temperature 240 °C
400000 cP

@Shear Rate 1000 1/s,
Temperature 464 °F
600000 cP

@Shear Rate 0.100 1/s,
Temperature 280 °C
600000 cP

@Shear Rate 0.100 1/s,
Temperature 536 °F
800000 cP

@Shear Rate 0.100 1/s,
Temperature 260 °C
800000 cP

@Shear Rate 0.100 1/s,
Temperature 500 °F
1.05e+6 cP

@Shear Rate 0.100 1/s,
Temperature 240 °C
1.05e+6 cP

@Shear Rate 0.100 1/s,
Temperature 464 °F
Viscosity Measurement 3.03
3.03
RSV formic acid, 1g/100ml; DSM method
Viscosity Test 196 cm³/g
196 cm³/g
Viscosity Number; ISO 307, 1157, 1628
Thickness 50.0 microns
1.97 mil
film
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 31.0 MPa
4500 psi
parallel; ISO 527-3
Film Elongation at Break, MD 350 %
350 %
parallel; ISO 527-3
Modulus of Elasticity 0.455 GPa
66.0 ksi
film; DSM-Method, 50 mm/min
Coefficient of Friction, Dynamic 1.0
1.0
film; ISO 8295
Coefficient of Friction, Static 1.2
1.2
film; ISO 8295
Tear Strength Test 32
32
Trouser tear resistance, parallel, film; ISO 6383-1
Film Tensile Strength at Break, MD 82.0 MPa
11900 psi
parallel; ISO 527-3
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C
50.0 µin/in-°F
ISO 11359-1/-2
Optical Properties Metric English Comments
Transmission, Visible 83 %
83 %
film; DSM method
Processing Properties Metric English Comments
Processing Temperature 270 °C
518 °F
Extruder Temperature
Die Temperature 270 °C
518 °F
Roll Temperature 110 °C
230 °F
Descriptive Properties Value Comments
Extrusion Type Cast Film
Puncture Resistance 1300 J/m
Film (DSM Method)