Material Notes:
Low/Medium Viscosity, Film Extrusion
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Water Vapor Transmission 35.0 g/m²/day

@Temperature 23.0 °C
2.25 g/100 in²/day

@Temperature 73.4 °F
at 85% r.h., film; DIS 15106-1/-3
Oxygen Transmission 1.30 cc-mm/m²-24hr-atm

@Temperature 23.0 °C
3.30 cc-mil/100 in²-24hr-atm

@Temperature 73.4 °F
at 0% r.h., film; DIS 15105-1/-2
1.90 cc-mm/m²-24hr-atm

@Temperature 23.0 °C
4.83 cc-mil/100 in²-24hr-atm

@Temperature 73.4 °F
at 85% r.h., film; DIS 15105-1/-2
Viscosity 410000 cP

@Temperature 260 °C
410000 cP

@Temperature 500 °F
Melt Viscosity; DSM method
200000 cP

@Shear Rate 1000 1/s,
Temperature 280 °C
200000 cP

@Shear Rate 1000 1/s,
Temperature 536 °F
250000 cP

@Shear Rate 1000 1/s,
Temperature 260 °C
250000 cP

@Shear Rate 1000 1/s,
Temperature 500 °F
300000 cP

@Shear Rate 1000 1/s,
Temperature 240 °C
300000 cP

@Shear Rate 1000 1/s,
Temperature 464 °F
350000 cP

@Shear Rate 0.100 1/s,
Temperature 280 °C
350000 cP

@Shear Rate 0.100 1/s,
Temperature 536 °F
475000 cP

@Shear Rate 0.100 1/s,
Temperature 260 °C
475000 cP

@Shear Rate 0.100 1/s,
Temperature 500 °F
650000 cP

@Shear Rate 0.100 1/s,
Temperature 240 °C
650000 cP

@Shear Rate 0.100 1/s,
Temperature 464 °F
Viscosity Measurement 2.7
2.7
RSV formic acid, 1g/100ml; DSM method
Viscosity Test 168 cm³/g
168 cm³/g
Viscosity Number; ISO 307, 1157, 1628
Thickness 50.0 microns
1.97 mil
film
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 32.0 MPa
4640 psi
parallel; ISO 527-3
Film Elongation at Break, MD 350 %
350 %
parallel; ISO 527-3
Modulus of Elasticity 0.460 GPa
66.7 ksi
film; DSM-Method, 50 mm/min
Coefficient of Friction, Dynamic 1.2
1.2
film; ISO 8295
Coefficient of Friction, Static 1.5
1.5
film; ISO 8295
Tear Strength Test 32
32
Trouser tear resistance, parallel, film; ISO 6383-1
Film Tensile Strength at Break, MD 80.0 MPa
11600 psi
parallel; ISO 527-3
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C
50.0 µin/in-°F
ISO 11359-1/-2
Specific Heat Capacity 1.55 J/g-°C

@Temperature 23.0 °C
0.370 BTU/lb-°F

@Temperature 73.4 °F
2.25 J/g-°C

@Temperature 20.0 - 150 °C
0.538 BTU/lb-°F

@Temperature 68.0 - 302 °F
Optical Properties Metric English Comments
Transmission, Visible 83 %
83 %
film; DSM method
Processing Properties Metric English Comments
Processing Temperature 270 °C
518 °F
Extruder Temperature
Die Temperature 270 °C
518 °F
Roll Temperature 110 °C
230 °F
Descriptive Properties Value Comments
Extrusion Type Cast Film
Puncture Resistance 1150 J/m
Film (DSM Method)