Crucible Steel 430 Chromium Steel
| Category | Metal , Ferrous Metal , Stainless Steel , T 400 Series Stainless Steel |
| Manufacturer | Crucible Steel |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Crucible Steel 430 Chromium Steel.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Crucible 430 is essentially a non-hardenable chromium steel which is adaptable for general purpose corrosion and heat resisting applications. It is prone to slight hardening by heat treatment. This grade is magnetic at all times. Information provided by Crucible Specialty Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 7.72 g/cc | 7.72 g/cc |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 160 | 160 | |
| Tensile Strength, Ultimate | 517 MPa | 75000 psi | |
| 27.6 MPa @Temperature 927 °C |
4000 psi @Temperature 1700 °F |
||
| 269 MPa @Temperature 538 °C |
39000 psi @Temperature 1000 °F |
||
| Tensile Strength, Yield | 310 MPa @Strain 0.200 % |
45000 psi @Strain 0.200 % |
|
| Elongation at Break | 30 % | 30 % | in 2" |
| Reduction of Area | 60 % | 60 % | |
| Creep Strength | 8.963 MPa @Temperature 704 °C |
1300 psi @Temperature 1300 °F |
|
| 58.6 MPa @Temperature 538 °C |
8500 psi @Temperature 1000 °F |
||
| Rupture Strength | 23.44 MPa @Temperature 649 °C, Time 3.60e+6 sec |
3400 psi @Temperature 1200 °F, Time 1000 hour |
|
| 34.47 MPa @Temperature 649 °C, Time 3.60e+6 sec |
5000 psi @Temperature 1200 °F, Time 1000 hour |
||
| 165.5 MPa @Temperature 482 °C, Time 3.60e+7 sec |
24000 psi @Temperature 900 °F, Time 10000 hour |
||
| 206.8 MPa @Temperature 482 °C, Time 3.60e+6 sec |
30000 psi @Temperature 900 °F, Time 1000 hour |
||
| Modulus of Elasticity | 200 GPa | 29000 ksi | |
| Izod Impact Unnotched | 54.2 J | 40.0 ft-lb |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 10.4 µm/m-°C @Temperature 0.000 - 100 °C |
5.80 µin/in-°F @Temperature 32.0 - 212 °F |
|
| 11.0 µm/m-°C @Temperature 0.000 - 316 °C |
6.10 µin/in-°F @Temperature 32.0 - 600 °F |
||
| 11.9 µm/m-°C @Temperature 0.000 - 649 °C |
6.60 µin/in-°F @Temperature 32.0 - 1200 °F |
||
| Specific Heat Capacity | 0.460 J/g-°C @Temperature 0.000 - 100 °C |
0.110 BTU/lb-°F @Temperature 32.0 - 212 °F |
|
| Thermal Conductivity | 22.65 W/m-K @Temperature 93.3 °C |
157.2 BTU-in/hr-ft²-°F @Temperature 200 °F |
|
| 26.28 W/m-K @Temperature 538 °C |
182.4 BTU-in/hr-ft²-°F @Temperature 1000 °F |
||
| Melting Point | 1430 - 1510 °C | 2600 - 2750 °F | |
| Solidus | 1430 °C | 2600 °F | |
| Liquidus | 1510 °C | 2750 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.12 % | <= 0.12 % | |
| Chromium, Cr | 16 - 18 % | 16 - 18 % | |
| Iron, Fe | >= 79.81 % | >= 79.81 % | As Remainder |
| Manganese, Mn | <= 1.0 % | <= 1.0 % | |
| Phosphorous, P | <= 0.040 % | <= 0.040 % | |
| Silicon, Si | <= 1.0 % | <= 1.0 % | |
| Sulfur, S | <= 0.030 % | <= 0.030 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.00005994 ohm-cm @Temperature 23.0 °C |
0.00005994 ohm-cm @Temperature 73.4 °F |