Covestro Makrolon® XT5010 Polycarbonate

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded
Manufacturer Covestro
Trade Name Makrolon®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Covestro Makrolon® XT5010 Polycarbonate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Easy processing• Low viscosity, easy releaseAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
Physical Properties Metric English Comments
Density 1.21 g/cc
0.0437 lb/in³
ISO 1183-1
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
50 mm/min; ISO 527-1,-2
Tensile Strength, Yield 75.0 MPa
10900 psi
50 mm/min; ISO 527-1,-2
Elongation at Break >= 50 %
>= 50 %
Nominal, 50 mm/min; ISO 527-1,-2
90 %
90 %
50 mm/min; b.o. ISO 527-1,-2
Elongation at Yield 5.0 %
5.0 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 2.70 GPa
392 ksi
1 mm/min; ISO 527-1,-2
Izod Impact, Notched (ISO) 8.00 kJ/m²

@Thickness 3.00 mm,
Temperature 23.0 °C
3.81 ft-lb/in²

@Thickness 0.118 in,
Temperature 73.4 °F
complete break; b.o. ISO 180-A
Charpy Impact Unnotched 22.0 J/cm²

@Temperature 23.0 °C
105 ft-lb/in²

@Temperature 73.4 °F
complete break; ISO 179-1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179-1eU
Thermal Properties Metric English Comments
Vicat Softening Point 112 °C

@Load 5.10 kg
234 °F

@Load 11.2 lb
50°C/h; ISO 306
114 °C

@Load 5.10 kg
237 °F

@Load 11.2 lb
120°C/h; ISO 306
UL RTI, Electrical 80.0 °C
176 °F
UL 746B
UL RTI, Mechanical with Impact 80.0 °C
176 °F
UL 746B
UL RTI, Mechanical without Impact 80.0 °C
176 °F
UL 746B
Flammability, UL94 V-2
V-2
Glow Wire Test 800 °C

@Thickness 0.750 mm
1470 °F

@Thickness 0.0295 in
GWIT; IEC 60695-2-13
825 °C

@Thickness 1.50 mm
1520 °F

@Thickness 0.0591 in
GWIT; IEC 60695-2-13
850 °C

@Thickness 3.00 mm
1560 °F

@Thickness 0.118 in
GWIT; IEC 60695-2-13
960 °C

@Thickness 0.750 mm
1760 °F

@Thickness 0.0295 in
GWFI; IEC 60695-2-12
960 °C

@Thickness 1.50 mm
1760 °F

@Thickness 0.0591 in
GWFI; IEC 60695-2-12
960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
GWFI; IEC 60695-2-12
Processing Properties Metric English Comments
Melt Temperature 260 °C
500 °F
Injection molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection molding; ISO 294
Injection Velocity 200 mm/sec
7.87 in/sec
ISO 294