Covestro Makrolon® GF8002* Polycarbonate, 15% Glass Filled

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 20% Glass Filled
Manufacturer	Covestro
Trade Name	Makrolon®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Covestro Makrolon® GF8002* Polycarbonate, 15% Glass Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

ISO 7391-PC,MR,(,,)-09-9,GF15Formerly Makrolon DP1-1882MVR (300 °C/1.2 kg) 9.5 cm3/10 min15 % Glass fiber reinforcedMedium viscosityEasy releaseInjection molding - Melt temperature 310 - 330 °CAvailable in opaque colors onlyPreprocessingMax. Water content

Physical Properties	Metric	English	Comments
Density	1.29 g/cc	0.0466 lb/in³	ISO 1183
	1.10 g/cc @Temperature 300 °C	0.0397 lb/in³ @Temperature 572 °F	Melt
Melt Flow	10 g/10 min @Load 1.20 kg, Temperature 300 °C	10 g/10 min @Load 2.65 lb, Temperature 572 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	45.0 MPa	6530 psi	ISO 527-1/-2
Elongation at Break	8.5 %	8.5 %	ISO 527-1/-2
Tensile Modulus	4.50 GPa	653 ksi	ISO 527-1/-2

Thermal Properties	Metric	English	Comments
Specific Heat Capacity	1.55 J/g-°C	0.370 BTU/lb-°F	Melt
Thermal Conductivity	0.198 W/m-K	1.37 BTU-in/hr-ft²-°F	Melt
Vicat Softening Point	144 °C	291 °F	50°C/h 50N; ISO 306

Processing Properties	Metric	English	Comments
Melt Temperature	300 °C	572 °F	Injection Molding; ISO 294
	310 - 330 °C	590 - 626 °F
Mold Temperature	80.0 - 130 °C	176 - 266 °F
	110 °C	230 °F	Injection Molding; ISO 10724
Ejection Temperature	140 °C	284 °F
Injection Velocity	200 mm/sec	7.87 in/sec	ISO 294

Descriptive Properties	Value	Comments
Availability	Asia Pacific
	Europe
	Near East/Africa
	South and Central America
Eff. thermal diffusivity (m²/s)	1.17E-07
Feature	Release agent
Form	Pellets
Process	Injection Molding

Users viewing this material also viewed the following: