Covestro Makrolon® FR 7087 Polycarbonate

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded , Polycarbonate, Unreinforced, Flame Retardant , Polycarbonate, UV Stabilized
Manufacturer	Covestro
Trade Name	Makrolon®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Covestro Makrolon® FR 7087 Polycarbonate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Flame retardant• Medium viscosity, easy release• UV stabilizedAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.

Physical Properties	Metric	English	Comments
Melt Flow	12 g/10 min @Load 1.20 kg, Temperature 300 °C	12 g/10 min @Load 2.65 lb, Temperature 572 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	75.0 MPa	10900 psi	50 mm/min; ISO 527-1,-2
Tensile Strength, Yield	75.0 MPa	10900 psi	50 mm/min; ISO 527-1,-2
Elongation at Break	100 %	100 %	50 mm/min; b.o. ISO 527-1,-2
Elongation at Yield	5.0 %	5.0 %	50 mm/min; ISO 527-1,-2
Tensile Modulus	2.50 GPa	363 ksi	1 mm/min; ISO 527-1,-2
Charpy Impact Unnotched	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179-1eU

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	118 °C	244 °F	ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi)	106 °C	223 °F	ISO 75-1,-2
UL RTI, Electrical	80.0 °C	176 °F	UL 746B
UL RTI, Mechanical with Impact	80.0 °C	176 °F	UL 746B
UL RTI, Mechanical without Impact	80.0 °C	176 °F	UL 746B
Flammability, UL94	V-2 @Thickness 1.50 mm	V-2 @Thickness 0.0591 in
	V-0 @Thickness 2.20 mm	V-0 @Thickness 0.0866 in
	5VA @Thickness 3.00 mm	5VA @Thickness 0.118 in	UL-94 5V
Glow Wire Test	930 °C @Thickness 1.50 mm	1710 °F @Thickness 0.0591 in	GWIT; IEC 60695-2-13
	960 °C @Thickness 2.20 mm	1760 °F @Thickness 0.0866 in	GWIT; IEC 60695-2-13
	960 °C @Thickness 3.00 mm	1760 °F @Thickness 0.118 in	GWIT; IEC 60695-2-13
	960 °C @Thickness 1.50 mm	1760 °F @Thickness 0.0591 in	GWFI; IEC 60695-2-12
	960 °C @Thickness 2.20 mm	1760 °F @Thickness 0.0866 in	GWFI; IEC 60695-2-12
	960 °C @Thickness 3.00 mm	1760 °F @Thickness 0.118 in	GWFI; IEC 60695-2-12

Optical Properties	Metric	English	Comments
Haze	0.90 % @Thickness 3.00 mm	0.90 % @Thickness 0.118 in	ISO 14782
Transmission, Visible	88 % @Thickness 3.00 mm	88 % @Thickness 0.118 in	ISO 13468-2

Processing Properties	Metric	English	Comments
Melt Temperature	290 °C	554 °F	Injection molding; ISO 294
Mold Temperature	80.0 °C	176 °F	Injection molding; ISO 294
Injection Velocity	200 mm/sec	7.87 in/sec	ISO 294

Users viewing this material also viewed the following: