Covestro Makrolon® 6465 Polycarbonate, Injection Grade

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant
Manufacturer	Covestro
Trade Name	Makrolon®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Covestro Makrolon® 6465 Polycarbonate, Injection Grade.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Medium viscosity, flame retardant injection molding with easy mold burning behavior.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.

Physical Properties	Metric	English	Comments
Density	1.20 g/cc	0.0434 lb/in³
Water Absorption	0.35 %	0.35 %	Saturation in water
Moisture Absorption at Equilibrium	0.15 %	0.15 %	Equilibrium at 50% RH
Water Absorption at Saturation	0.35 %	0.35 %
Melt Flow	9.5 g/10 min @Load 1.20 kg, Temperature 300 °C	9.5 g/10 min @Load 2.65 lb, Temperature 572 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	63.0 MPa	9140 psi
Elongation at Break	>= 50 %	>= 50 %	Nominal
Elongation at Yield	6.0 %	6.0 %
Tensile Modulus	2.40 GPa	348 ksi
Charpy Impact Unnotched	NB	NB
Tensile Creep Modulus, 1 hour	2200 MPa	319000 psi
Tensile Creep Modulus, 1000 hours	1900 MPa	276000 psi

Thermal Properties	Metric	English
CTE, linear, Parallel to Flow	70.0 µm/m-°C @Temperature 20.0 °C	38.9 µin/in-°F @Temperature 68.0 °F
CTE, linear, Transverse to Flow	70.0 µm/m-°C @Temperature 20.0 °C	38.9 µin/in-°F @Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	136 °C	277 °F
Deflection Temperature at 1.8 MPa (264 psi)	128 °C	262 °F
Vicat Softening Point	144 °C	291 °F
Glass Transition Temp, Tg	148 °C	298 °F
UL RTI, Electrical	125 °C @Thickness 1.10 mm	257 °F @Thickness 0.0433 in
UL RTI, Mechanical with Impact	110 °C @Thickness 1.10 mm	230 °F @Thickness 0.0433 in
UL RTI, Mechanical without Impact	125 °C @Thickness 1.10 mm	257 °F @Thickness 0.0433 in
Flammability, UL94	V-0 @Thickness 1.20 mm	V-0 @Thickness 0.0472 in
	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in
Oxygen Index	35 %	35 %

Electrical Properties	Metric	English	Comments
Electrical Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm
Surface Resistance	1.00e+15 ohm	1.00e+15 ohm
Dielectric Constant	3.0 @Frequency 100 Hz	3.0 @Frequency 100 Hz
	3.0 @Frequency 1e+6 Hz	3.0 @Frequency 1e+6 Hz
Dielectric Strength	30.0 kV/mm	762 kV/in
Dissipation Factor	0.0010 @Frequency 100 Hz	0.0010 @Frequency 100 Hz
	0.0090 @Frequency 1e+6 Hz	0.0090 @Frequency 1e+6 Hz
Arc Resistance	60 - 120 sec @Thickness 6.00 mm	60 - 120 sec @Thickness 0.236 in	UL Rating PLC 6 (60-120 sec)
Comparative Tracking Index	275 V	275 V
Hot Wire Ignition, HWI	30 - 60 sec @Thickness 1.10 mm	30 - 60 sec @Thickness 0.0433 in	UL Rating PLC 2 (30-60 sec)
High Amp Arc Ignition, HAI	60 - 120 arcs @Thickness 1.10 mm	60 - 120 arcs @Thickness 0.0433 in	UL Rating PLC 1 (60-120 arcs)
High Voltage Arc-Tracking Rate, HVTR	<= 10.0 mm/min @Thickness 6.00 mm	<= 0.394 in/min @Thickness 0.236 in	UL Rating PLC 0 (<10 mm/min.)