Covestro Bayflex® 110-50 Polyurethane

Category Polymer , Thermoset , Polyurethane, TS , Thermoset Polyurethane, Liquid
Manufacturer Covestro
Trade Name Bayflex®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Covestro Bayflex® 110-50 Polyurethane.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
Water Absorption 2.8 %
2.8 %
240 hours
Water Absorption at Saturation 2.8 %
2.8 %
240 hours
Linear Mold Shrinkage 0.013 cm/cm
0.013 in/in
Mechanical Properties Metric English Comments
Hardness, Shore D 58
58
ASTM D2240
Tensile Strength, Ultimate 24.0 MPa
3480 psi
ASTM D638
Tensile Strength, Yield 18.0 MPa
2610 psi
Elongation at Break 250 %
250 %
ASTM D638/D412
Elongation at Yield 8.0 %
8.0 %
Tensile Modulus 1.10 GPa
160 ksi
Flexural Modulus 0.400 GPa
58.0 ksi
ASTM D790
Izod Impact, Notched 5.90 J/cm
11.1 ft-lb/in
ASTM D256
Charpy Impact Unnotched NB
NB
0.772 J/cm²

@Temperature -30.0 °C
3.67 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 3.48 J/cm²
16.6 ft-lb/in²
Tear Strength 79.0 kN/m
451 pli
Die C; ASTM D624
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 54.0 µm/m-°C

@Temperature 20.0 °C
30.0 µin/in-°F

@Temperature 68.0 °F
CTE, linear, Transverse to Flow 164 µm/m-°C

@Temperature 20.0 °C
91.1 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 148 °C
298 °F
Flammability, UL94 HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in