Covestro Baydur® 110 FR Polyurethane

Category	Polymer , Thermoset , Polyurethane, TS , Thermoset Polyurethane, Liquid
Manufacturer	Covestro
Trade Name	Baydur®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Covestro Baydur® 110 FR Polyurethane.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Rigid microcellular RIM polyurethane material. Fast demold times; self releasing; long flow paths possible, therefore suitable for production of large moldings. Parts are injected through only one gate.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.

Physical Properties	Metric	English	Comments
Density	1.05 g/cc	0.0379 lb/in³
Water Absorption	2.0 %	2.0 %	Saturation in water
Water Absorption at Saturation	2.0 %	2.0 %

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	50.0 MPa	7250 psi
Elongation at Break	12 %	12 %
Tensile Modulus	2.00 GPa	290 ksi
Charpy Impact Unnotched	5.00 J/cm²	23.8 ft-lb/in²

Thermal Properties	Metric	English
CTE, linear, Parallel to Flow	90.0 µm/m-°C @Temperature 20.0 °C	50.0 µin/in-°F @Temperature 68.0 °F
CTE, linear, Transverse to Flow	90.0 µm/m-°C @Temperature 20.0 °C	50.0 µin/in-°F @Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	115 °C	239 °F
Deflection Temperature at 1.8 MPa (264 psi)	90.0 °C	194 °F
Vicat Softening Point	135 °C	275 °F
Flammability, UL94	V-0 @Thickness 6.00 mm	V-0 @Thickness 0.236 in

Electrical Properties	Metric	English
Electrical Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm
Surface Resistance	1.00e+13 ohm	1.00e+13 ohm
Dielectric Strength	15.0 kV/mm	381 kV/in