Covestro Bayblend® W85 XF* Polycarbonate + ASA

Category	Polymer , Thermoplastic , ASA Polymer , Polycarbonate (PC) , Polycarbonate/ASA Alloy, Unreinforced
Manufacturer	Covestro
Trade Name	Bayblend®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Covestro Bayblend® W85 XF* Polycarbonate + ASA.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Developmental product(PC+ASA) blendinjection molding grade with improved weather resistanceoptimized heat ageing stabilityhigh heat resistanceVicat/B 120 = 132 °CPreprocessingMax. Water content

Physical Properties	Metric	English	Comments
Density	1.16 g/cc	0.0419 lb/in³	ISO 1183
Melt Flow	31 g/10 min @Load 5.00 kg, Temperature 260 °C	31 g/10 min @Load 11.0 lb, Temperature 500 °F	estimated from MVR using room temperature density; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	62.0 MPa	8990 psi	ISO 527-1/-2
Elongation at Yield	4.9 %	4.9 %	ISO 527-1/-2
Tensile Modulus	2.45 GPa	355 ksi	ISO 527-1/-2

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	65.0 µm/m-°C	36.1 µin/in-°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	68.0 µm/m-°C	37.8 µin/in-°F	ISO 11359-1/-2
Deflection Temperature at 0.46 MPa (66 psi)	127 °C	261 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	109 °C	228 °F	ISO 75-1/-2
Vicat Softening Point	130 °C	266 °F	50°C/h 50N; ISO 306

Processing Properties	Metric	English	Comments
Melt Temperature	240 - 280 °C	464 - 536 °F
	260 °C	500 °F	Injection Molding; ISO 294
Mold Temperature	60.0 - 80.0 °C	140 - 176 °F
	80.0 °C	176 °F	Injection Molding; ISO 10724
Injection Velocity	240 mm/sec	9.45 in/sec	ISO 294

Descriptive Properties	Value	Comments
Availability	Asia Pacific
	Europe
	India
	Near East/Africa
	South and Central America
Feature	Heat stabilised or stable to heat
	Light stabilised or stable to light
	Release agent
	U.V. stabilised or stable to weather
Form	Pellets
Process	Injection Molding