Covestro Bayblend® T65 HI PC/ABS Blend

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Covestro
Trade Name Bayblend®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Covestro Bayblend® T65 HI PC/ABS Blend.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Main characteristics:• High toughness even at low temperatures• High dimensional accuracy and stability• Good paintability• Good flowabilityGrade characteristics:• Improve low temperature impact strength and chemical resistance for automotive parts• Extrusion/extrusion blow molding• Electroplating applicationsAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
Physical Properties Metric English Comments
Density 1.11 g/cc
0.0401 lb/in³
ISO 1183-1
Moisture Absorption at Equilibrium 0.20 %
0.20 %
ISO 62, 50% RH
Water Absorption at Saturation 0.70 %
0.70 %
ISO 62
Viscosity 300000 cP

@Shear Rate 1000 1/s,
Temperature 260 °C
300000 cP

@Shear Rate 1000 1/s,
Temperature 500 °F
melt viscosity; b.o. ISO 11443-A
Linear Mold Shrinkage, Flow 0.0065 - 0.0085 cm/cm

@Thickness 3.00 mm
0.0065 - 0.0085 in/in

@Thickness 0.118 in
150x105x3mm; b.o. ISO 2577
Linear Mold Shrinkage, Transverse 0.0065 - 0.0085 cm/cm

@Thickness 3.00 mm
0.0065 - 0.0085 in/in

@Thickness 0.118 in
150x105x3mm; b.o. ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 46.0 MPa
6670 psi
50 mm/min; ISO 527-1,-2
Tensile Strength, Yield 48.0 MPa
6960 psi
50 mm/min; ISO 527-1,-2
Elongation at Break >= 50 %
>= 50 %
50 mm/min; b.o. ISO 527-1,-2
Elongation at Yield 4.5 %
4.5 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 2.00 GPa
290 ksi
1 mm/min; ISO 527-1,-2
Izod Impact, Notched (ISO) 38.0 kJ/m²

@Temperature -30.0 °C
18.1 ft-lb/in²

@Temperature -22.0 °F
ISO 180-A
48.0 kJ/m²

@Temperature 23.0 °C
22.8 ft-lb/in²

@Temperature 73.4 °F
ISO 180-A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 180-U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 180-U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
50.0 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1,-2
CTE, linear, Transverse to Flow 95.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
52.8 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1,-2
Deflection Temperature at 0.46 MPa (66 psi) 120 °C
248 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 99.0 °C
210 °F
ISO 75-1,-2
Vicat Softening Point 118 °C

@Load 5.10 kg
244 °F

@Load 11.2 lb
50°C/h; ISO 306
120 °C

@Load 5.10 kg
248 °F

@Load 11.2 lb
120°C/h; ISO 306
Flammability, UL94 HB

@Thickness 0.850 mm
HB

@Thickness 0.0335 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
IEC 60093
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
IEC 60093
Dielectric Constant 2.9

@Frequency 1.00e+6 Hz
2.9

@Frequency 1.00e+6 Hz
IEC 60250
3.0

@Frequency 100 Hz
3.0

@Frequency 100 Hz
IEC 60250
Dielectric Strength 35.0 kV/mm

@Thickness 1.00 mm
889 kV/in

@Thickness 0.0394 in
IEC 60243-1
Dissipation Factor 0.0025

@Frequency 100 Hz
0.0025

@Frequency 100 Hz
IEC 60250
0.0085

@Frequency 1.00e+6 Hz
0.0085

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 275 V
275 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 260 °C
500 °F
Injection molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection molding; ISO 294
Injection Velocity 240 mm/sec
9.45 in/sec
ISO 294