Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Covestro Bayblend® R-FR610 Polycarbonate Recyclate Blend

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant
Manufacturer Covestro
Trade Name Bayblend®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Covestro Bayblend® R-FR610 Polycarbonate Recyclate Blend.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Main characteristics:• High toughness even at low temperatures• High dimensional accuracy and stability• Good paintability• Good flowabilityGrade characteristics:• Flame retardantAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183-1
Moisture Absorption at Equilibrium 0.20 %
0.20 %
ISO 62, 50% RH
Water Absorption at Saturation 0.50 %
0.50 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.00 mm
0.0050 - 0.0070 in/in

@Thickness 0.118 in
150x105x3mm; b.o. ISO 2577
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Thickness 3.00 mm
0.0050 - 0.0070 in/in

@Thickness 0.118 in
150x105x3mm; b.o. ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 45.0 MPa
6530 psi
50 mm/min; ISO 527-1,-2
Tensile Strength, Yield 55.0 MPa
7980 psi
50 mm/min; ISO 527-1,-2
Elongation at Break 30 %
30 %
50 mm/min; b.o. ISO 527-1,-2
Elongation at Yield 4.0 %
4.0 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 2.60 GPa
377 ksi
1 mm/min; ISO 527-1,-2
Izod Impact, Notched (ISO) 10.0 kJ/m²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 180-A
40.0 kJ/m²

@Temperature 23.0 °C
19.0 ft-lb/in²

@Temperature 73.4 °F
ISO 180-A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 180-U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 76.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
42.2 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1,-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
44.4 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1,-2
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C
203 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
ISO 75-1,-2
Vicat Softening Point 108 °C

@Load 5.10 kg
226 °F

@Load 11.2 lb
50°C/h; ISO 306
110 °C

@Load 5.10 kg
230 °F

@Load 11.2 lb
120°C/h; ISO 306
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
5VA

@Thickness 3.00 mm
5VA

@Thickness 0.118 in
UL 94-5V
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
IEC 60093
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
IEC 60093
Dielectric Constant 3.1

@Frequency 1.00e+6 Hz
3.1

@Frequency 1.00e+6 Hz
IEC 60250
3.2

@Frequency 100 Hz
3.2

@Frequency 100 Hz
IEC 60250
Dielectric Strength 30.0 kV/mm

@Thickness 1.00 mm
762 kV/in

@Thickness 0.0394 in
IEC 60243-1
Dissipation Factor 0.0030

@Frequency 100 Hz
0.0030

@Frequency 100 Hz
IEC 60250
0.0085

@Frequency 1.00e+6 Hz
0.0085

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 300 V
300 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 240 °C
464 °F
Injection molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection molding; ISO 294
Injection Velocity 240 mm/sec
9.45 in/sec
ISO 294
Copyright © lookpolymers.com All Rights Reserved