Covestro Bayblend® KU 2-1500 Polycarbonate/ABS Blend

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Covestro
Trade Name Bayblend®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Covestro Bayblend® KU 2-1500 Polycarbonate/ABS Blend.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Flame retardant extrusion grade.Applications: Bulky parts for DT-copying machines.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
Physical Properties Metric English Comments
Density 1.21 g/cc
0.0437 lb/in³
Water Absorption 0.70 %
0.70 %
Saturation in water
Moisture Absorption at Equilibrium 0.20 %
0.20 %
Equilibrium at 50% RH
Water Absorption at Saturation 0.70 %
0.70 %
Melt Flow 5.0 g/10 min

@Load 5.00 kg,
Temperature 260 °C
5.0 g/10 min

@Load 11.0 lb,
Temperature 500 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 55.0 MPa
7980 psi
Elongation at Break >= 50 %
>= 50 %
Nominal
Elongation at Yield 5.0 %
5.0 %
Tensile Modulus 2.40 GPa
348 ksi
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 124 °C
255 °F
Deflection Temperature at 1.8 MPa (264 psi) 107 °C
225 °F
Vicat Softening Point 128 °C
262 °F
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
Oxygen Index 34 %
34 %
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Dielectric Constant 3.1

@Frequency 1e+6 Hz
3.1

@Frequency 1e+6 Hz
3.2

@Frequency 100 Hz
3.2

@Frequency 100 Hz
Dielectric Strength 30.0 kV/mm
762 kV/in
Dissipation Factor 0.0027

@Frequency 100 Hz
0.0027

@Frequency 100 Hz
0.0082

@Frequency 1e+6 Hz
0.0082

@Frequency 1e+6 Hz
Comparative Tracking Index 350 V
350 V