Covestro Bayblend® KU 2-1473 Polycarbonate/ABS Blend  (discontinued **)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Covestro Bayblend® KU 2-1473 Polycarbonate/ABS Blend  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Matter surfaces than standard grades; injection molding.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This product was discontinued prior to the separation.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
Water Absorption 0.70 %
0.70 %
Saturation in water
Moisture Absorption at Equilibrium 0.20 %
0.20 %
Equilibrium at 50% RH
Water Absorption at Saturation 0.70 %
0.70 %
Melt Flow 10 g/10 min

@Load 5.00 kg,
Temperature 260 °C
10 g/10 min

@Load 11.0 lb,
Temperature 500 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 45.0 MPa
6530 psi
Elongation at Break >= 50 %
>= 50 %
Nominal
Elongation at Yield 4.0 %
4.0 %
Tensile Modulus 2.10 GPa
305 ksi
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 81.0 µm/m-°C

@Temperature 20.0 °C
45.0 µin/in-°F

@Temperature 68.0 °F
CTE, linear, Transverse to Flow 86.0 µm/m-°C

@Temperature 20.0 °C
47.8 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 126 °C
259 °F
Deflection Temperature at 1.8 MPa (264 psi) 105 °C
221 °F
Vicat Softening Point 128 °C
262 °F
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Oxygen Index 23 %
23 %
Electrical Properties Metric English Comments
Electrical Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Dielectric Constant 2.0

@Frequency 100 Hz
2.0

@Frequency 100 Hz
2.9

@Frequency 1e+6 Hz
2.9

@Frequency 1e+6 Hz
Dielectric Strength 24.0 kV/mm
610 kV/in
Dissipation Factor 0.0040

@Frequency 100 Hz
0.0040

@Frequency 100 Hz
0.0070

@Frequency 1e+6 Hz
0.0070

@Frequency 1e+6 Hz
Comparative Tracking Index 300 V
300 V