Covestro Bayblend® KU 2-1468 Polycarbonate/ABS Blend
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Covestro |
| Trade Name | Bayblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Covestro Bayblend® KU 2-1468 Polycarbonate/ABS Blend.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | |
| Water Absorption | 0.70 % | 0.70 % | Saturation in water |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | Equilibrium at 50% RH |
| Water Absorption at Saturation | 0.70 % | 0.70 % | |
| Melt Flow | 14 g/10 min @Load 5.00 kg, Temperature 260 °C |
14 g/10 min @Load 11.0 lb, Temperature 500 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | |
| Elongation at Break | >= 50 % | >= 50 % | Nominal |
| Elongation at Yield | 5.0 % | 5.0 % | |
| Tensile Modulus | 2.60 GPa | 377 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 75.0 µm/m-°C @Temperature 20.0 °C |
41.7 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 20.0 °C |
44.4 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 112 °C | 234 °F | |
| Vicat Softening Point | 134 °C | 273 °F | |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| Oxygen Index | 30 % | 30 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 3.2 @Frequency 1e+6 Hz |
3.2 @Frequency 1e+6 Hz |
|
| 3.3 @Frequency 100 Hz |
3.3 @Frequency 100 Hz |
||
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | |
| Dissipation Factor | 0.0027 @Frequency 100 Hz |
0.0027 @Frequency 100 Hz |
|
| 0.0082 @Frequency 1e+6 Hz |
0.0082 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 225 V | 225 V |
Users viewing this material also viewed the following:
- Plaskolite West Optix® CA-75 General Purpose Acrylic Resin
- Reliance Industries Polypropylene - Calcium carbonate filled
- IDI Composites C-103 Thermoset Polyester, Molding
- Lotus Nano Paint NAP 201 Fast Dry Nano-paint
- IRPC Polimaxx Porene SR101 Acrylonitrile Butadiene Styrene
- Trelleborg Neoprene® C627 Chloroprene
- Dow TONE™ 0310 Polyol
- BASF Ultramid® KR 4365 G5 BK 00100 35% Glass Filled PA6/6T FR (Dry)
- Beijing Ranger Chem PBT-201-G10 272 Flame Retarding FR PBT
- Axiall 8710 Moldings & Extrusions Flexible PVC
Copyright © lookpolymers.com All Rights Reserved