- Covestro Bayblend® KU 2-1466 Polycarbonate/ABS Blend
Covestro Bayblend® KU 2-1466 Polycarbonate/ABS Blend
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC) |
| Manufacturer | Covestro |
| Trade Name | Bayblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Covestro Bayblend® KU 2-1466 Polycarbonate/ABS Blend.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant grade with 20% glass fiber reinforcement, high stiffness.Applications: Electrical industry.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | |
| Water Absorption | 0.70 % | 0.70 % | Saturation in water |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | Equilibrium at 50% RH |
| Water Absorption at Saturation | 0.70 % | 0.70 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 79.0 MPa | 11500 psi | |
| Elongation at Break | 2.0 % | 2.0 % | |
| Tensile Modulus | 5.80 GPa | 841 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 28.0 µm/m-°C @Temperature 20.0 °C |
15.6 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | 67.0 µm/m-°C @Temperature 20.0 °C |
37.2 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | |
| Vicat Softening Point | 134 °C | 273 °F | |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| Oxygen Index | 33 % | 33 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 3.2 @Frequency 1e+6 Hz |
3.2 @Frequency 1e+6 Hz |
|
| 3.3 @Frequency 100 Hz |
3.3 @Frequency 100 Hz |
||
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | |
| Dissipation Factor | 0.0020 @Frequency 100 Hz |
0.0020 @Frequency 100 Hz |
|
| 0.0070 @Frequency 1e+6 Hz |
0.0070 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 150 V | 150 V |