Covestro Bayblend® KL 1-1427 Polycarbonate/ABS Blend

Category	Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC)
Manufacturer	Covestro
Trade Name	Bayblend®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Covestro Bayblend® KL 1-1427 Polycarbonate/ABS Blend.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Glass fiber reinforced grade (30%) with high stiffness.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.

Physical Properties	Metric	English	Comments
Density	1.31 g/cc	0.0473 lb/in³
Water Absorption	0.60 %	0.60 %	Saturation in water
Moisture Absorption at Equilibrium	0.20 %	0.20 %	Equilibrium at 50% RH
Water Absorption at Saturation	0.60 %	0.60 %

Mechanical Properties	Metric	English	Comments
Elongation at Break	2.0 %	2.0 %
Tensile Modulus	8.00 GPa	1160 ksi

Thermal Properties	Metric	English
CTE, linear, Parallel to Flow	29.0 µm/m-°C @Temperature 20.0 °C	16.1 µin/in-°F @Temperature 68.0 °F
CTE, linear, Transverse to Flow	52.0 µm/m-°C @Temperature 20.0 °C	28.9 µin/in-°F @Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	130 °C	266 °F
Deflection Temperature at 1.8 MPa (264 psi)	125 °C	257 °F
Vicat Softening Point	131 °C	268 °F
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
Oxygen Index	24 %	24 %

Electrical Properties	Metric	English
Electrical Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm
Dielectric Constant	3.0 @Frequency 100 Hz	3.0 @Frequency 100 Hz
	3.2 @Frequency 1e+6 Hz	3.2 @Frequency 1e+6 Hz
Dielectric Strength	30.0 kV/mm	762 kV/in
Dissipation Factor	0.0020 @Frequency 100 Hz	0.0020 @Frequency 100 Hz
	0.0090 @Frequency 1e+6 Hz	0.0090 @Frequency 1e+6 Hz
Comparative Tracking Index	200 V	200 V