Covestro Bayblend® FR3015 PC/ABS Blend

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Covestro
Trade Name Bayblend®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Covestro Bayblend® FR3015 PC/ABS Blend.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Main characteristics:• High toughness even at low temperatures• High dimensional accuracy and stability• Good paintability• Good flowabilityGrade characteristics:• Flame-retardant• Injection moldingAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183-1
Viscosity 330000 cP

@Shear Rate 1000 1/s,
Temperature 260 °C
330000 cP

@Shear Rate 1000 1/s,
Temperature 500 °F
melt viscosity; b.o. ISO 11443-A
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.00 mm
0.0050 - 0.0070 in/in

@Thickness 0.118 in
150x105x3mm; b.o. ISO 2577
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Thickness 3.00 mm
0.0050 - 0.0070 in/in

@Thickness 0.118 in
150x105x3mm; b.o. ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
7250 psi
50 mm/min; ISO 527-1,-2
Tensile Strength, Yield 60.0 MPa
8700 psi
50 mm/min; ISO 527-1,-2
Elongation at Break >= 50 %
>= 50 %
50 mm/min; b.o. ISO 527-1,-2
Elongation at Yield 4.5 %
4.5 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 2.70 GPa
392 ksi
1 mm/min; ISO 527-1,-2
Izod Impact, Notched (ISO) 35.0 kJ/m²

@Temperature 23.0 °C
16.7 ft-lb/in²

@Temperature 73.4 °F
ISO 180-A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 180-U
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 99.0 °C
210 °F
ISO 75-1,-2
Vicat Softening Point 119 °C

@Load 5.10 kg
246 °F

@Load 11.2 lb
120°C/h; ISO 306
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
5VB

@Thickness 2.00 mm
5VB

@Thickness 0.0787 in
Glow Wire Test 960 °C

@Thickness 1.50 mm
1760 °F

@Thickness 0.0591 in
GWFI; IEC 60695-2-12
Electrical Properties Metric English Comments
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
IEC 60093
Processing Properties Metric English Comments
Melt Temperature 260 °C
500 °F
Injection molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection molding; ISO 294
Injection Velocity 240 mm/sec
9.45 in/sec
ISO 294