Covestro Bayblend® FR 3011 Polycarbonate + ABS, Flame Retardant Grade

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Covestro
Trade Name Bayblend®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Covestro Bayblend® FR 3011 Polycarbonate + ABS, Flame Retardant Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Injection molding gradegood flowhigh heat resistanceVicat/B 120 temperature = 118 °CUL-listing 94 V-0 (1.5 mm) antimony-, chlorine- and bromine-free flame retardantglow wire test (GWFI): 960 °C (2.0 mm)no juicinggood light stabilityPreprocessingMax. Water content
Physical Properties Metric English Comments
Density 1.19 g/cc
0.0430 lb/in³
ISO 1183
Water Absorption 0.50 %
0.50 %
Similar to ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
Similar to ISO 62
Melt Flow 20 g/10 min

@Load 5.00 kg,
Temperature 240 °C
20 g/10 min

@Load 11.0 lb,
Temperature 464 °F
estimated from MVR using room temperature density; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 65.0 MPa
9430 psi
ISO 527-1/-2
Elongation at Yield 4.0 %
4.0 %
ISO 527-1/-2
Tensile Modulus 2.60 GPa
377 ksi
ISO 527-1/-2
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 108 °C
226 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
ISO 75-1/-2
Vicat Softening Point 116 °C
241 °F
50°C/h 50N; ISO 306
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
IEC 60695-11-10
5VB

@Thickness 2.00 mm
5VB

@Thickness 0.0787 in
IEC 60695-11-20
Processing Properties Metric English Comments
Melt Temperature 240 °C
464 °F
Injection Molding; ISO 294
240 - 270 °C
464 - 518 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
80.0 °C
176 °F
Injection Molding; ISO 10724
Injection Velocity 240 mm/sec
9.45 in/sec
ISO 294
Descriptive Properties Value Comments
Availability Asia Pacific
Europe
India
Near East/Africa
South and Central America
Feature Release agent
Form Pellets
Process Injection Molding