- Cossa Polimeri ESTAPROP H 05100 GFC Polypropylene, 50% Glass Filled
Cossa Polimeri ESTAPROP H 05100 GFC Polypropylene, 50% Glass Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 50% Glass Fiber Filler |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTAPROP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTAPROP H 05100 GFC Polypropylene, 50% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PP homopolymer 50% chemically coupled glass fiberExcellent stiffness, excellent impact strengthInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D 955 |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa | 16000 psi | ASTM D 638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D 638 |
| Tensile Modulus | 12.5 GPa | 1810 ksi | ASTM D 638 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D 790 |
| Izod Impact, Notched | 1.10 J/cm @Temperature -20.0 °C |
2.06 ft-lb/in @Temperature -4.00 °F |
ASTM D 638 |
| 1.30 J/cm @Temperature 0.000 °C |
2.44 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 | |
| 1.50 J/cm @Temperature 23.0 °C |
2.81 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 155 °C | 311 °F | 120°C/hr; ASTM D 648 |
| Vicat Softening Point | 145 °C @Load 5.00 kg |
293 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
Users viewing this material also viewed the following:
- PolyOne Synprene™ RT-5190 RoHS Black Styrene Butadiene Block Copolymer (SBC)
- Techmer ES HiFill® PP GF/M30 CC BK 30% Glass/Mineral Filled
- Samsung Cheil Industries Infino® AR-6508 PBT/PET, Glass Filled
- Samsung Cheil Industries Starex® SF-301H Expandable Polystyrene (EPS) FR
- Teknor Apex Flexalloy® 3500-80 Polyvinyl Chloride Elastomer
- A. Schulman SCHULAMID® 66 MK4015H 40% Glass Fiber/Mineral Reinforced, Heat Stabilized Nylon 66
- A. Schulman INVISION™ VX-5170UE Soft Touch Polyolefin Thermoplastic
- Hippe EP GC 21 Woven Glass Cloth Reinforced Epoxy Resin - Round, Rolled Tube
- BASF Lupranate® 5020 Isocyanate
- 3M Scotch-Weld™ CA100 Instant Adhesive
Copyright © lookpolymers.com All Rights Reserved