Cossa Polimeri ESTADIENE 3520 Acrylonitrile Butadiene Styrene

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
Manufacturer Cossa Polimeri S.r.L.
Trade Name ESTADIENE
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Cossa Polimeri ESTADIENE 3520 Acrylonitrile Butadiene Styrene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ABS with high impact resistanceHigh melt flow rate, high impact resistance at low temperature, excellent processability and surface appearanceInformation provided by Cossa Polimeri S.r.l.
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ASTM D 792
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
ASTM D 955
Melt Flow 25 g/10 min

@Load 10.0 kg,
Temperature 220 °C
25 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 35.0 MPa
5080 psi
ASTM D 638
Tensile Strength, Yield 40.0 MPa
5800 psi
ASTM D 638
Elongation at Break 25 %
25 %
ASTM D 638
Flexural Modulus 2.10 GPa
305 ksi
ASTM D 790
Izod Impact, Notched 3.00 J/cm

@Temperature 0.000 °C
5.62 ft-lb/in

@Temperature 32.0 °F
ASTM D 638
3.50 J/cm

@Temperature 23.0 °C
6.56 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Thermal Properties Metric English Comments
Vicat Softening Point 96.0 °C

@Load 5.00 kg
205 °F

@Load 11.0 lb
50°C/hr; ASTM D 1525
105 °C

@Load 0.999 kg
221 °F

@Load 2.20 lb
50°C/hr; ASTM D 1525
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Glow Wire Test 650 °C

@Thickness 2.00 mm
1200 °F

@Thickness 0.0787 in
I.E.C. 695-2-1