Cossa Polimeri ESTADIENE 1218 V0/B Flame Retardant ABS

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
Manufacturer Cossa Polimeri S.r.L.
Trade Name ESTADIENE
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Cossa Polimeri ESTADIENE 1218 V0/B Flame Retardant ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Acrylonitrile Butadiene StyreneFlame retardant class V0, PBDE free, good impact resistance, excellent processability, good surface appearanceInformation provided by Cossa Polimeri S.r.l.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ASTM D 792
Linear Mold Shrinkage 0.0030 - 0.0060 cm/cm
0.0030 - 0.0060 in/in
ASTM D 955
Melt Flow 45 g/10 min

@Load 10.0 kg,
Temperature 220 °C
45 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa
5800 psi
ASTM D 638
Tensile Strength, Yield 45.0 MPa
6530 psi
ASTM D 638
Elongation at Break 5.0 %
5.0 %
ASTM D 638
Flexural Modulus 2.50 GPa
363 ksi
ASTM D 790
Izod Impact, Notched 0.900 J/cm

@Temperature 0.000 °C
1.69 ft-lb/in

@Temperature 32.0 °F
ASTM D 638
1.20 J/cm

@Temperature 23.0 °C
2.25 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Thermal Properties Metric English Comments
Vicat Softening Point 85.0 °C

@Load 5.00 kg
185 °F

@Load 11.0 lb
50°C/hr; ASTM D 1525
95.0 °C

@Load 0.999 kg
203 °F

@Load 2.20 lb
50°C/hr; ASTM D 1525
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
V-0

@Thickness 3.20 mm
V-0

@Thickness 0.126 in
Glow Wire Test 960 °C
1760 °F
I.E.C. 695-2-1