Cossa Polimeri ESTACARB 1560 V0 HF Flame Retardant Polycarbonate

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant
Manufacturer Cossa Polimeri S.r.L.
Trade Name ESTACARB
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Cossa Polimeri ESTACARB 1560 V0 HF Flame Retardant Polycarbonate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Flame retardant class V0, opaque, antimony, chlorine and bromine free, high impact resistance, high thermal resistance, good melt flow rate, good processability, good light resistanceInformation provided by Cossa Polimeri S.r.l.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ASTM D 792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D 955
Melt Flow 15 g/10 min

@Load 1.20 kg,
Temperature 300 °C
15 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
ASTM D 638
Tensile Strength, Yield 65.0 MPa
9430 psi
ASTM D 638
Elongation at Break >= 50 %
>= 50 %
ASTM D 638
Flexural Modulus 2.50 GPa
363 ksi
ASTM D 790
Izod Impact, Notched 5.50 J/cm

@Temperature 0.000 °C
10.3 ft-lb/in

@Temperature 32.0 °F
ASTM D 638
6.00 J/cm

@Temperature 23.0 °C
11.2 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Thermal Properties Metric English Comments
Hot Ball Pressure Test 135 °C
275 °F
I.E.C. 335-1
Vicat Softening Point 146 °C

@Load 5.00 kg
295 °F

@Load 11.0 lb
50°C/hr; ASTM D 1525
148 °C

@Load 0.999 kg
298 °F

@Load 2.20 lb
50°C/hr; ASTM D 1525
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
V-0

@Thickness 3.20 mm
V-0

@Thickness 0.126 in
Glow Wire Test 960 °C
1760 °F
I.E.C. 695-2-1