Cossa Polimeri ESTABLEND CR Polycarbonate ABS Blend

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Cossa Polimeri S.r.L.
Trade Name ESTABLEND
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Cossa Polimeri ESTABLEND CR Polycarbonate ABS Blend.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polycarbonate and Acrylonitrile Butadiene Styrene blend for chromium plating, painting and metallizationGood impact resistance, good thermal resistanceInformation provided by Cossa Polimeri S.r.l.
Physical Properties Metric English Comments
Density 1.11 g/cc
0.0401 lb/in³
ASTM D 792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D 955
Melt Flow 15 g/10 min

@Load 5.00 kg,
Temperature 260 °C
15 g/10 min

@Load 11.0 lb,
Temperature 500 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 32.0 MPa
4640 psi
ASTM D 638
Tensile Strength, Yield 40.0 MPa
5800 psi
ASTM D 638
Elongation at Break 50 %
50 %
ASTM D 638
Flexural Modulus 2.00 GPa
290 ksi
ASTM D 790
Izod Impact, Notched 4.10 J/cm

@Temperature 0.000 °C
7.68 ft-lb/in

@Temperature 32.0 °F
ASTM D 638
4.50 J/cm

@Temperature 23.0 °C
8.43 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Thermal Properties Metric English Comments
Vicat Softening Point 110 °C

@Load 5.00 kg
230 °F

@Load 11.0 lb
50°C/hr; ASTM D 1525
123 °C

@Load 0.999 kg
253 °F

@Load 2.20 lb
50°C/hr; ASTM D 1525
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in