- Cossa Polimeri ESTABLEND 4500 T V0 Flame Retardant PC - ABS
Cossa Polimeri ESTABLEND 4500 T V0 Flame Retardant PC - ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTABLEND |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTABLEND 4500 T V0 Flame Retardant PC - ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PC - ABS BlendFlame retardant class V0, PBDE free, with halogens, high impact resistance, high thermal resistance, good processabilityInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D 955 |
| Melt Flow | 20 g/10 min @Load 5.00 kg, Temperature 260 °C |
20 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 40.0 MPa | 5800 psi | ASTM D 638 |
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | ASTM D 638 |
| Elongation at Break | 80 % | 80 % | ASTM D 638 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ASTM D 790 |
| Izod Impact, Notched | 4.50 J/cm @Temperature 0.000 °C |
8.43 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 |
| 5.00 J/cm @Temperature 23.0 °C |
9.37 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | 105 °C | 221 °F | I.E.C. 335-1 |
| Vicat Softening Point | 125 °C @Load 5.00 kg |
257 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| 135 °C @Load 0.999 kg |
275 °F @Load 2.20 lb |
50°C/hr; ASTM D 1525 | |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
||
| Glow Wire Test | 960 °C | 1760 °F | I.E.C. 695-2-1 |
Users viewing this material also viewed the following:
- Hong Kun Group HBTU Pharmaceutical Intermediate
- Huntsman HZ 3441 OU-66 Phenalkamine Hardener
- Michelman® Michem® Prime 4983-40R Ethylene acrylic acid dispersion
- KaMin Hydragloss® 90 Clay
- Ineos ABS Triax® 1120 ABS + Polyamide Blend (Conditioned)
- SABIC Innovative Plastics NORYL GTX GTX918W PPE+PS+PA (Asia Pacific)
- Hexcel® IM4 Carbon Fiber (12,000 Filaments)
- ChevronTexaco RPM® SAE 15W-40 Heavy Duty Motor Oil
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR N774 Filler
Copyright © lookpolymers.com All Rights Reserved