Constellium PLAN 5754 Aluminum Rolled Plate

Category Metal , Nonferrous Metal , Aluminum Alloy , 5000 Series Aluminum Alloy
Manufacturer Constellium
Trade Name PLAN
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Constellium PLAN 5754 Aluminum Rolled Plate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Rolled plates in 5754 PLAN are optimized for minimum residual stress and improved dimensional tolerances. 5754 PLAN is mainly used for low stressed mechanical components, manufactured by intensive machining. Typical applications include parts for packaging machines.Information provided by manufacturer
Physical Properties Metric English Comments
Density 2.67 g/cc
0.0965 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 76

@Thickness 20.0 - 150 mm
76

@Thickness 0.787 - 5.91 in
77

@Thickness 4.00 - 20.0 mm
77

@Thickness 0.157 - 0.787 in
Tensile Strength 190 - 240 MPa

@Thickness 4.00 - 12.5 mm
27600 - 34800 psi

@Thickness 0.157 - 0.492 in
Temper H111; Standard EN 485-2
>= 255 MPa

@Thickness 12.5 - 100 mm
>= 37000 psi

@Thickness 0.492 - 3.94 in
Temper H111; Standard EN 485-2
295 MPa

@Thickness 4.00 - 20.0 mm
42800 psi

@Thickness 0.157 - 0.787 in
Typical Strength
295 MPa

@Thickness 20.0 - 150 mm
42800 psi

@Thickness 0.787 - 5.91 in
Typical Strength
Tensile Strength, Yield >= 80.0 MPa

@Strain 0.200 %,
Thickness 4.00 - 12.5 mm
>= 11600 psi

@Strain 0.200 %,
Thickness 0.157 - 0.492 in
Temper H111; Standard EN 485-2
>= 105 MPa

@Strain 0.200 %,
Thickness 12.5 - 100 mm
>= 15200 psi

@Strain 0.200 %,
Thickness 0.492 - 3.94 in
Temper H111; Standard EN 485-2
140 MPa

@Strain 0.200 %,
Thickness 20.0 - 150 mm
20300 psi

@Strain 0.200 %,
Thickness 0.787 - 5.91 in
Typical Strength
150 MPa

@Strain 0.200 %,
Thickness 4.00 - 20.0 mm
21800 psi

@Strain 0.200 %,
Thickness 0.157 - 0.787 in
Typical Strength
Elongation at Break >= 12 %

@Thickness 12.5 - 100 mm
>= 12 %

@Thickness 0.492 - 3.94 in
Temper H111; Standard EN 485-2
>= 18 %

@Thickness 4.00 - 12.5 mm
>= 18 %

@Thickness 0.157 - 0.492 in
Temper H111; Standard EN 485-2
22 %

@Thickness 20.0 - 150 mm
22 %

@Thickness 0.787 - 5.91 in
Typical Elongation; Standard EN 485-2
23 %

@Thickness 4.00 - 20.0 mm
23 %

@Thickness 0.157 - 0.787 in
Typical Elongation; Standard EN 485-2
Modulus of Elasticity 70.0 GPa
10200 ksi
Thermal Properties Metric English Comments
CTE, linear 23.8 µm/m-°C

@Temperature 20.0 - 100 °C
13.2 µin/in-°F

@Temperature 68.0 - 212 °F
Thermal Conductivity 130 - 140 W/m-K
902 - 972 BTU-in/hr-ft²-°F
Component Elements Properties Metric English Comments
Aluminum, Al 94.35 - 97.4 %
94.35 - 97.4 %
as balance
Chromium, Cr <= 0.30 %
<= 0.30 %
Copper, Cu <= 0.10 %
<= 0.10 %
Iron, Fe <= 0.40 %
<= 0.40 %
Magnesium, Mg 2.6 - 3.6 %
2.6 - 3.6 %
Manganese, Mn <= 0.50 %
<= 0.50 %
Silicon, Si <= 0.40 %
<= 0.40 %
Zinc, Zn <= 0.20 %
<= 0.20 %
Zr+Ti <= 0.15 %
<= 0.15 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000400 - 0.00000520 ohm-cm
0.00000400 - 0.00000520 ohm-cm