Constellium PLAN 5083 Aluminum Rolled Plate

Category Metal , Nonferrous Metal , Aluminum Alloy , 5000 Series Aluminum Alloy
Manufacturer Constellium
Trade Name PLAN
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Constellium PLAN 5083 Aluminum Rolled Plate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Rolled plates in 5083 PLAN are optimized for minimum residual stress and improved dimensional tolerances. 5083 PLAN is mainly used for low stressed mechanical components, manufactured by intensive machining. Typical applications include parts for printing, packaging and food conditioning machines.Information provided by manufacturer
Physical Properties Metric English Comments
Density 2.66 g/cc
0.0961 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 76

@Thickness 20.0 - 150 mm
 76

@Thickness 0.787 - 5.91 in
77

@Thickness 5.00 - 20.0 mm
 77

@Thickness 0.197 - 0.787 in
Tensile Strength >= 255 MPa

@Thickness 120 - 150 mm
 >= 37000 psi

@Thickness 4.72 - 5.91 in
 Temper H111; Standard EN 485-2
>= 260 MPa

@Thickness 80.0 - 120 mm
 >= 37700 psi

@Thickness 3.15 - 4.72 in
 Temper H111; Standard EN 485-2
>= 270 MPa

@Thickness 6.30 - 12.5 mm
 >= 39200 psi

@Thickness 0.248 - 0.492 in
 Temper H111; Standard EN 485-2
>= 270 MPa

@Thickness 12.5 - 50.0 mm
 >= 39200 psi

@Thickness 0.492 - 1.97 in
 Temper H111; Standard EN 485-2
>= 270 MPa

@Thickness 50.0 - 80.0 mm
 >= 39200 psi

@Thickness 1.97 - 3.15 in
 Temper H111; Standard EN 485-2
>= 275 MPa

@Thickness 5.00 - 6.30 mm
 >= 39900 psi

@Thickness 0.197 - 0.248 in
 Temper H111; Standard EN 485-2
295 MPa

@Thickness 5.00 - 20.0 mm
 42800 psi

@Thickness 0.197 - 0.787 in
 Typical Strength
295 MPa

@Thickness 20.0 - 150 mm
 42800 psi

@Thickness 0.787 - 5.91 in
 Typical Strength
Tensile Strength, Yield >= 105 MPa

@Strain 0.200 %,
Thickness 120 - 150 mm
 >= 15200 psi

@Strain 0.200 %,
Thickness 4.72 - 5.91 in
 Temper H111; Standard EN 485-2
>= 110 MPa

@Strain 0.200 %,
Thickness 80.0 - 120 mm
 >= 16000 psi

@Strain 0.200 %,
Thickness 3.15 - 4.72 in
 Temper H111; Standard EN 485-2
>= 115 MPa

@Strain 0.200 %,
Thickness 6.30 - 12.5 mm
 >= 16700 psi

@Strain 0.200 %,
Thickness 0.248 - 0.492 in
 Temper H111; Standard EN 485-2
>= 115 MPa

@Strain 0.200 %,
Thickness 12.5 - 50.0 mm
 >= 16700 psi

@Strain 0.200 %,
Thickness 0.492 - 1.97 in
 Temper H111; Standard EN 485-2
>= 115 MPa

@Strain 0.200 %,
Thickness 50.0 - 80.0 mm
 >= 16700 psi

@Strain 0.200 %,
Thickness 1.97 - 3.15 in
 Temper H111; Standard EN 485-2
>= 125 MPa

@Strain 0.200 %,
Thickness 5.00 - 6.30 mm
 >= 18100 psi

@Strain 0.200 %,
Thickness 0.197 - 0.248 in
 Temper H111; Standard EN 485-2
140 MPa

@Strain 0.200 %,
Thickness 20.0 - 150 mm
 20300 psi

@Strain 0.200 %,
Thickness 0.787 - 5.91 in
 Typical Strength
150 MPa

@Strain 0.200 %,
Thickness 5.00 - 20.0 mm
 21800 psi

@Strain 0.200 %,
Thickness 0.197 - 0.787 in
 Typical Strength
Elongation at Break >= 12 %

@Thickness 80.0 - 120 mm
 >= 12 %

@Thickness 3.15 - 4.72 in
 Temper H111; Standard EN 485-2
>= 12 %

@Thickness 120 - 150 mm
 >= 12 %

@Thickness 4.72 - 5.91 in
 Temper H111; Standard EN 485-2
>= 14 %

@Thickness 50.0 - 80.0 mm
 >= 14 %

@Thickness 1.97 - 3.15 in
 Temper H111; Standard EN 485-2
>= 15 %

@Thickness 5.00 - 6.30 mm
 >= 15 %

@Thickness 0.197 - 0.248 in
 Temper H111; Standard EN 485-2
>= 15 %

@Thickness 12.5 - 50.0 mm
 >= 15 %

@Thickness 0.492 - 1.97 in
 Temper H111; Standard EN 485-2
>= 16 %

@Thickness 6.30 - 12.5 mm
 >= 16 %

@Thickness 0.248 - 0.492 in
 Temper H111; Standard EN 485-2
22 %

@Thickness 20.0 - 150 mm
 22 %

@Thickness 0.787 - 5.91 in
 Typical Elongation
23 %

@Thickness 5.00 - 20.0 mm
 23 %

@Thickness 0.197 - 0.787 in
 Typical Elongation
Modulus of Elasticity 71.0 GPa
10300 ksi
Thermal Properties Metric English Comments
CTE, linear 23.8 µm/m-°C

@Temperature 20.0 - 100 °C
 13.2 µin/in-°F

@Temperature 68.0 - 212 °F
Thermal Conductivity 105 - 120 W/m-K
729 - 833 BTU-in/hr-ft²-°F
Component Elements Properties Metric English Comments
Aluminum, Al 92.55 - 95.55 %
92.55 - 95.55 %
as balance
Chromium, Cr 0.050 - 0.25 %
0.050 - 0.25 %
Copper, Cu <= 0.10 %
<= 0.10 %
Iron, Fe <= 0.40 %
<= 0.40 %
Magnesium, Mg 4.0 - 4.9 %
4.0 - 4.9 %
Manganese, Mn 0.40 - 1.0 %
0.40 - 1.0 %
Silicon, Si <= 0.40 %
<= 0.40 %
Zinc, Zn <= 0.25 %
<= 0.25 %
Zr+Ti <= 0.15 %
<= 0.15 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000580 - 0.00000660 ohm-cm
0.00000580 - 0.00000660 ohm-cm