Constellium Fibral® Cast Aluminum Sliced Plate

Category Metal , Nonferrous Metal , Aluminum Alloy , 5000 Series Aluminum Alloy , Aluminum Casting Alloy
Manufacturer Constellium
Trade Name Fibral®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Constellium Fibral® Cast Aluminum Sliced Plate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Fibral® has been specifically developed for low–pressure processing (thermoforming, RTM) of plastics and their composites. The material can also be used for prototype injection moulds. The material properties are enhanced by its stringent casting process which considerably reduces porosity throughout the thickness of the plate.Information provided by manufacturer
Physical Properties Metric English Comments
Density 2.66 g/cc
0.0961 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 70

@Thickness 150 - 500 mm
70

@Thickness 5.91 - 19.7 in
70

@Thickness 500 - 600 mm
70

@Thickness 19.7 - 23.6 in
Tensile Strength >= 210 MPa

@Thickness 150 - 500 mm
>= 30500 psi

@Thickness 5.91 - 19.7 in
Temper O3
>= 210 MPa

@Thickness 500 - 600 mm
>= 30500 psi

@Thickness 19.7 - 23.6 in
Temper O3
235 MPa

@Thickness 150 - 500 mm
34100 psi

@Thickness 5.91 - 19.7 in
Typical Strength
235 MPa

@Thickness 500 - 600 mm
34100 psi

@Thickness 19.7 - 23.6 in
Typical Strength
Tensile Strength, Yield >= 110 MPa

@Strain 0.200 %,
Thickness 150 - 500 mm
>= 16000 psi

@Strain 0.200 %,
Thickness 5.91 - 19.7 in
Temper O3
>= 110 MPa

@Strain 0.200 %,
Thickness 500 - 600 mm
>= 16000 psi

@Strain 0.200 %,
Thickness 19.7 - 23.6 in
Temper O3
115 MPa

@Strain 0.200 %,
Thickness 150 - 500 mm
16700 psi

@Strain 0.200 %,
Thickness 5.91 - 19.7 in
Typical Strength
115 MPa

@Strain 0.200 %,
Thickness 500 - 600 mm
16700 psi

@Strain 0.200 %,
Thickness 19.7 - 23.6 in
Typical Strength
Elongation at Break >= 5.0 %

@Thickness 150 - 500 mm
>= 5.0 %

@Thickness 5.91 - 19.7 in
Temper O3
>= 5.0 %

@Thickness 500 - 600 mm
>= 5.0 %

@Thickness 19.7 - 23.6 in
Temper O3
9.5 %

@Thickness 150 - 500 mm
9.5 %

@Thickness 5.91 - 19.7 in
Typical Elongation
9.5 %

@Thickness 500 - 600 mm
9.5 %

@Thickness 19.7 - 23.6 in
Typical Elongation
Modulus of Elasticity 71.0 GPa
10300 ksi
Thermal Properties Metric English Comments
CTE, linear 23.8 µm/m-°C

@Temperature 20.0 - 100 °C
13.2 µin/in-°F

@Temperature 68.0 - 212 °F
Thermal Conductivity 105 - 120 W/m-K
729 - 833 BTU-in/hr-ft²-°F
Component Elements Properties Metric English Comments
Aluminum, Al 92.55 - 95.55 %
92.55 - 95.55 %
as balance
Chromium, Cr 0.050 - 0.25 %
0.050 - 0.25 %
Copper, Cu <= 0.10 %
<= 0.10 %
Iron, Fe <= 0.40 %
<= 0.40 %
Magnesium, Mg 4.0 - 4.9 %
4.0 - 4.9 %
Manganese, Mn 0.40 - 1.0 %
0.40 - 1.0 %
Silicon, Si <= 0.40 %
<= 0.40 %
Zinc, Zn <= 0.25 %
<= 0.25 %
Zr+Ti <= 0.15 %
<= 0.15 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000590 - 0.00000660 ohm-cm
0.00000590 - 0.00000660 ohm-cm