Constellium ALPLAN® 6082 Rolled Precision Aluminum Plate, Milled Both Sides

Category Metal , Nonferrous Metal , Aluminum Alloy , 6000 Series Aluminum Alloy
Manufacturer Constellium
Trade Name ALPLAN®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Constellium ALPLAN® 6082 Rolled Precision Aluminum Plate, Milled Both Sides.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Precision plates in ALPLAN® 6082 are milled on both sides and have a very low level of residual stress, thus avoiding excessive deformation during machining. Thanks to its very good dimensional stability and the elimination of surface milling operations, ALPLAN® 6082 plates enable to realize significant cost and time savings in machining, when compared to normal rolled plates.Information provided by manufacturer
Physical Properties Metric English Comments
Density 2.70 g/cc
0.0975 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 105

@Thickness 9.90 - 25.0 mm
 105

@Thickness 0.390 - 0.984 in
105

@Thickness 25.0 - 60.0 mm
 105

@Thickness 0.984 - 2.36 in
105

@Thickness 60.0 - 140 mm
 105

@Thickness 2.36 - 5.51 in
Tensile Strength >= 276 MPa

@Thickness 100 - 140 mm
 >= 40000 psi

@Thickness 3.94 - 5.51 in
 Temper T651; Standard EN 485-2
>= 295 MPa

@Thickness 12.5 - 60.0 mm
 >= 42800 psi

@Thickness 0.492 - 2.36 in
 Temper T651; Standard EN 485-2
>= 295 MPa

@Thickness 60.0 - 100 mm
 >= 42800 psi

@Thickness 2.36 - 3.94 in
 Temper T651; Standard EN 485-2
>= 300 MPa

@Thickness 9.90 - 12.5 mm
 >= 43500 psi

@Thickness 0.390 - 0.492 in
 Temper T651; Standard EN 485-2
350 MPa

@Thickness 9.90 - 25.0 mm
 50800 psi

@Thickness 0.390 - 0.984 in
 Typical Strength
350 MPa

@Thickness 25.0 - 60.0 mm
 50800 psi

@Thickness 0.984 - 2.36 in
 Typical Strength
350 MPa

@Thickness 60.0 - 140 mm
 50800 psi

@Thickness 2.36 - 5.51 in
 Typical Strength
Tensile Strength, Yield >= 240 MPa

@Strain 0.200 %,
Thickness 12.5 - 60.0 mm
 >= 34800 psi

@Strain 0.200 %,
Thickness 0.492 - 2.36 in
 Temper T651; Standard EN 485-2
>= 240 MPa

@Strain 0.200 %,
Thickness 60.0 - 100 mm
 >= 34800 psi

@Strain 0.200 %,
Thickness 2.36 - 3.94 in
 Temper T651; Standard EN 485-2
>= 240 MPa

@Strain 0.200 %,
Thickness 100 - 140 mm
 >= 34800 psi

@Strain 0.200 %,
Thickness 3.94 - 5.51 in
 Temper T651; Standard EN 485-2
>= 255 MPa

@Strain 0.200 %,
Thickness 9.90 - 12.5 mm
 >= 37000 psi

@Strain 0.200 %,
Thickness 0.390 - 0.492 in
 Temper T651; Standard EN 485-2
305 MPa

@Strain 0.200 %,
Thickness 9.90 - 25.0 mm
 44200 psi

@Strain 0.200 %,
Thickness 0.390 - 0.984 in
 Typical Strength
310 MPa

@Strain 0.200 %,
Thickness 25.0 - 60.0 mm
 45000 psi

@Strain 0.200 %,
Thickness 0.984 - 2.36 in
 Typical Strength
310 MPa

@Strain 0.200 %,
Thickness 60.0 - 140 mm
 45000 psi

@Strain 0.200 %,
Thickness 2.36 - 5.51 in
 Typical Strength
Elongation at Break >= 6.0 %

@Thickness 100 - 140 mm
 >= 6.0 %

@Thickness 3.94 - 5.51 in
 Temper T651; Standard EN 485-2
>= 7.0 %

@Thickness 60.0 - 100 mm
 >= 7.0 %

@Thickness 2.36 - 3.94 in
 Temper T651; Standard EN 485-2
>= 8.0 %

@Thickness 12.5 - 60.0 mm
 >= 8.0 %

@Thickness 0.492 - 2.36 in
 Temper T651; Standard EN 485-2
>= 9.0 %

@Thickness 9.90 - 12.5 mm
 >= 9.0 %

@Thickness 0.390 - 0.492 in
 Temper T651; Standard EN 485-2
11 %

@Thickness 9.90 - 25.0 mm
 11 %

@Thickness 0.390 - 0.984 in
 Typical Elongation
11 %

@Thickness 25.0 - 60.0 mm
 11 %

@Thickness 0.984 - 2.36 in
 Typical Elongation
11 %

@Thickness 60.0 - 140 mm
 11 %

@Thickness 2.36 - 5.51 in
 Typical Elongation
Modulus of Elasticity 69.0 GPa
10000 ksi
Thermal Properties Metric English Comments
CTE, linear 23.4 µm/m-°C

@Temperature 20.0 - 100 °C
 13.0 µin/in-°F

@Temperature 68.0 - 212 °F
Thermal Conductivity 150 - 170 W/m-K
1040 - 1180 BTU-in/hr-ft²-°F
Temper T651
Component Elements Properties Metric English Comments
Aluminum, Al 95.45 - 98.3 %
95.45 - 98.3 %
as balance
Chromium, Cr <= 0.25 %
<= 0.25 %
Copper, Cu <= 0.10 %
<= 0.10 %
Iron, Fe <= 0.50 %
<= 0.50 %
Magnesium, Mg 0.60 - 1.2 %
0.60 - 1.2 %
Manganese, Mn 0.40 - 1.0 %
0.40 - 1.0 %
Silicon, Si 0.70 - 1.3 %
0.70 - 1.3 %
Zinc, Zn <= 0.20 %
<= 0.20 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000360 - 0.00000420 ohm-cm
0.00000360 - 0.00000420 ohm-cm
Temper T651