- HOME
- POLYMER SEARCH
- Thermoplastic
- Acetal (POM)
- Acetal Copolymer, Aramid Fiber Filled
- Clariant Renol POMSP0001 Acetal Copolymer, Aramid Fiber, PTFE Lubricated
Clariant Renol POMSP0001 Acetal Copolymer, Aramid Fiber, PTFE Lubricated
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Aramid Fiber Filled , Acetal Copolymer, PTFE Filled |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol POMSP0001 Acetal Copolymer, Aramid Fiber, PTFE Lubricated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.018 cm/cm | 0.018 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 51.7 MPa | 7500 psi | ASTM D638 |
| Elongation at Break | 12 % | 12 % | ASTM D638 |
| Flexural Yield Strength | 75.8 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 2.55 GPa | 370 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm @Temperature 22.8 °C |
1.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 216 °C | 360 - 420 °F | |
| Mold Temperature | 79.4 - 107 °C | 175 - 225 °F | |
| Dry Time | 2 - 4 hour @Temperature 121 °C |
2 - 4 hour @Temperature 250 °F |
to ensure moisture level is less than 0.15% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CP8930 PC+ABS
- SABIC Innovative Plastics Lexan® EXL1182T PC Copolymer (Europe-Africa-Middle East)
- NOVA Chemicals Sclair® FPr017-D Octene LLDPE Film Resin
- LyondellBasell DEXFLEX® 727 TPO
- A. Schulman PP 1407L-01 Polypropylene High-Impact Copolymer Polypropylene
- Tra-Con Tra-Duct 2705 Room Temperature Conductive Nickel Epoxy Adhesive
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 40 PHR Non-Black, Soft Clay
- E-Polymers EFLEX® I1020 Ionomer
- E-Polymers EFLEX® S1040 General
Copyright © lookpolymers.com All Rights Reserved