Chosun Refractories MMCT-85 Special Castable

Category Ceramic , Oxide , Aluminum Oxide
Manufacturer Chosun Refractories
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chosun Refractories MMCT-85 Special Castable.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
Mechanical Properties Metric English Comments
Modulus of Rupture 0.0073575 GPa

@Temperature 110 °C,
Time 86400 sec
1.0671 ksi

@Temperature 230 °F,
Time 24.0 hour
0.00981 GPa

@Temperature 1350 °C,
Time 10800 sec
1.42 ksi

@Temperature 2460 °F,
Time 3.00 hour
0.014715 GPa

@Temperature 1500 °C,
Time 10800 sec
2.1343 ksi

@Temperature 2730 °F,
Time 3.00 hour
Compressive Strength 39.2 MPa

@Temperature 110 °C,
Time 86400 sec
5690 psi

@Temperature 230 °F,
Time 24.0 hour
Cold Crushing Strength
68.6 MPa

@Temperature 1350 °C,
Time 10800 sec
9960 psi

@Temperature 2460 °F,
Time 3.00 hour
Cold Crushing Strength
78.5 MPa

@Temperature 1500 °C,
Time 10800 sec
11400 psi

@Temperature 2730 °F,
Time 3.00 hour
Cold Crushing Strength
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 1700 °C
3090 °F
limited
Shrinkage -0.100 %

@Temperature 1350 °C,
Time 10800 sec
-0.100 %

@Temperature 2460 °F,
Time 3.00 hour
-0.0300 %

@Temperature 110 °C,
Time 86400 sec
-0.0300 %

@Temperature 230 °F,
Time 24.0 hour
0.40 %

@Temperature 1500 °C,
Time 10800 sec
0.40 %

@Temperature 2730 °F,
Time 3.00 hour
Component Elements Properties Metric English Comments
Al2O3 85 %
85 %
SiO2 3.0 %
3.0 %
Descriptive Properties Value Comments
Installation Method Casting, Vibrating
Material Required for Estimating(kg/?) 2,800
Water Required for Casting(%) 7.5