- Chosun Refractories HSC-18SC Dense and High-Strength Castable, Superdense
Chosun Refractories HSC-18SC Dense and High-Strength Castable, Superdense
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories HSC-18SC Dense and High-Strength Castable, Superdense.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.021582 GPa @Temperature 110 °C, Time 86400 sec |
3.1303 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.02943 GPa @Temperature 1000 °C, Time 10800 sec |
4.269 ksi @Temperature 1830 °F, Time 3.00 hour |
||
| 0.03924 GPa @Temperature 1500 °C, Time 10800 sec |
5.691 ksi @Temperature 2730 °F, Time 3.00 hour |
||
| Compressive Strength | 127 MPa @Temperature 110 °C, Time 86400 sec |
18500 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| 137 MPa @Temperature 1000 °C, Time 10800 sec |
19900 psi @Temperature 1830 °F, Time 3.00 hour |
Cold Crushing Strength | |
| 177 MPa @Temperature 1500 °C, Time 10800 sec |
25600 psi @Temperature 2730 °F, Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 1800 °C | 3270 °F | limited |
| Shrinkage | -0.430 % @Temperature 1500 °C, Time 10800 sec |
-0.430 % @Temperature 2730 °F, Time 3.00 hour |
|
| -0.0300 % @Temperature 110 °C, Time 86400 sec |
-0.0300 % @Temperature 230 °F, Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 93 % | 93 % | |
| CaO | 2.0 % | 2.0 % | |
| SiO2 | 3.0 % | 3.0 % |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 - 600 min | 2.00 - 10.0 hour | Setting Time |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Vibrating | |
| Material Required for Estimating(kg/?) | 3,250 | |
| Water Required for Casting(%) | 3.7 |
Users viewing this material also viewed the following:
- PolyOne Bergamid™ B70 W25 G45 H Polyamide 6 (Nylon 6)
- Polimersan Plastics POLITEF® (PTFE) with 60% Bronze
- M. Holland Company IS410 Polystyrene, High Impact (discontinued **)
- Lord Adhesives Thermosetâ„¢ LS 213-9 Unfilled Epoxy Encapsulant
- Haynes 282® Nickel Alloy Autogenously Welded Sheet
- Loctite® Output™ 315 Acrylic Adhesive
- CP-Polymer-Technik Wellamid® 6600 GV 40 HWCP 40% Glass Fiber Nylon 66, Heat Stabilized, Conditioned
- Chosun Refractories CTC-65SH Monolithic Refractories for Ladle and Tundish
- A. Schulman ComAlloy Comtuf® 604 Nylon 6/6, Impact Modified, Flow Enhanced
- Bhansali Engineering Santron IMS 2000 SAN Resin
Copyright © lookpolymers.com All Rights Reserved