Chosun Refractories HSC-16RA Dense and High-Strength Castable, Credens
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories HSC-16RA Dense and High-Strength Castable, Credens.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.00981 GPa @Temperature 110 °C, Time 86400 sec |
1.42 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.010791 GPa @Temperature 1000 °C, Time 10800 sec |
1.5651 ksi @Temperature 1830 °F, Time 3.00 hour |
||
| 0.010791 GPa @Temperature 1500 °C, Time 10800 sec |
1.5651 ksi @Temperature 2730 °F, Time 3.00 hour |
||
| Compressive Strength | 61.8 MPa @Temperature 110 °C, Time 86400 sec |
8960 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| 63.7 MPa @Temperature 1000 °C, Time 10800 sec |
9250 psi @Temperature 1830 °F, Time 3.00 hour |
Cold Crushing Strength | |
| 68.6 MPa @Temperature 1500 °C, Time 10800 sec |
9960 psi @Temperature 2730 °F, Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 1600 °C | 2910 °F | limited |
| Shrinkage | -0.500 % @Temperature 1500 °C, Time 10800 sec |
-0.500 % @Temperature 2730 °F, Time 3.00 hour |
|
| -0.0500 % @Temperature 110 °C, Time 86400 sec |
-0.0500 % @Temperature 230 °F, Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 58 % | 58 % | |
| CaO | 2.0 % | 2.0 % | |
| SiO2 | 37 % | 37 % |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 - 600 min | 2.00 - 10.0 hour | Setting Time |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Vibrating, Casting | |
| Material Required for Estimating(kg/?) | 2,700 | |
| Water Required for Casting(%) | 6 |
Users viewing this material also viewed the following:
- Osprey Metals 420/MA Stainless Steel Powder (Grade 90% - 22)
- Abatron 85083 A/B Filled Potting Compound (discontinued **)
- Pyrotek MT-29L Microporous Ladle Lining Insulation
- Daelim H&L Plavis G15 Aromatic Polyimide, 15% Graphite Filled, Direct Formed (Unverified Data**)
- Intercontinental Polymers 216 PET Polymer Type - Semi-Dull, Polyester Pellets
- Samsung Cheil Industries Infino® HM-3301GL PC, Glass Filled High Impact
- Teknor Apex TEKBOND® MP 1728 Thermoplastic Elastomer
- A. Schulman ComAlloy Comtuf® 523 Polycarbonate/Styrenic Alloy
- Solvay RHODAFAC® RS-710 E Surfactant
Copyright © lookpolymers.com All Rights Reserved