Chosun Refractories HACT-155 High Alumina Castables
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories HACT-155 High Alumina Castables.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.0024525 - 0.0063765 GPa @Temperature 1000 °C, Time 10800 sec |
0.35571 - 0.92485 ksi @Temperature 1830 °F, Time 3.00 hour |
|
| 0.002943 - 0.006867 GPa @Temperature 1350 °C, Time 10800 sec |
0.4269 - 0.9960 ksi @Temperature 2460 °F, Time 3.00 hour |
||
| 0.002943 - 0.006867 GPa @Temperature 110 °C, Time 86400 sec |
0.4269 - 0.9960 ksi @Temperature 230 °F, Time 24.0 hour |
||
| Compressive Strength | 14.7 - 24.5 MPa @Temperature 1000 °C, Time 10800 sec |
2130 - 3560 psi @Temperature 1830 °F, Time 3.00 hour |
Cold Crushing Strength |
| 19.6 - 29.4 MPa @Temperature 1350 °C, Time 10800 sec |
2840 - 4270 psi @Temperature 2460 °F, Time 3.00 hour |
Cold Crushing Strength | |
| 19.6 - 29.4 MPa @Temperature 110 °C, Time 86400 sec |
2840 - 4270 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.74442 W/m-K @Temperature 260 °C |
5.1579 BTU-in/hr-ft²-°F @Temperature 500 °F |
|
| 0.84910 W/m-K @Temperature 540 °C |
5.8832 BTU-in/hr-ft²-°F @Temperature 1000 °F |
||
| 0.9305 W/m-K @Temperature 800 °C |
6.447 BTU-in/hr-ft²-°F @Temperature 1470 °F |
||
| Maximum Service Temperature, Air | 1550 °C | 2820 °F | limited |
| Shrinkage | -0.0600 % @Temperature 110 °C, Time 86400 sec |
-0.0600 % @Temperature 230 °F, Time 24.0 hour |
|
| 0.50 % @Temperature 1350 °C, Time 10800 sec |
0.50 % @Temperature 2460 °F, Time 3.00 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 48 % | 48 % | |
| SiO2 | 44 % | 44 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Casting, Troweling | |
| Material Required for Estimating(kg/?) | 2,150 | |
| Water Required for Casting(%) | 11.0 |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Hypalon® 40 Chlorosulfonated Polyethylene Rubber, Peroxide Cured Carbon Black Filled Compound
- Techmer ES Electrablend® ABS 03009
- SABIC Innovative Plastics Ultem ATX103R PEI+PCE (Europe-Africa-Middle East)
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 60 PHR Carbon Black, N-220 (ISAF)
- DuPont Teijin Films Mylar® M461 Polyester Film, 500 Gauge
- A. Schulman ComAlloy Hiloy® 612 Nylon 6, Glass Reinforced, UL
- BASF Ultraform® S2320 003 POM
- ExxonMobil Escorene® HD-8761 HDPE, Rotational Molding Powder (discontinued **)
Copyright © lookpolymers.com All Rights Reserved