Chosun Refractories HACT-150 High Alumina Castables
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories HACT-150 High Alumina Castables.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.0024525 - 0.0063765 GPa @Temperature 110 °C, Time 86400 sec |
0.35571 - 0.92485 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.0024525 - 0.0063765 GPa @Temperature 1000 °C, Time 10800 sec |
0.35571 - 0.92485 ksi @Temperature 1830 °F, Time 3.00 hour |
||
| 0.001962 - 0.006867 GPa @Temperature 1350 °C, Time 10800 sec |
0.2846 - 0.9960 ksi @Temperature 2460 °F, Time 3.00 hour |
||
| Compressive Strength | 14.7 - 24.5 MPa @Temperature 110 °C, Time 86400 sec |
2130 - 3560 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| 14.7 - 24.5 MPa @Temperature 1000 °C, Time 10800 sec |
2130 - 3560 psi @Temperature 1830 °F, Time 3.00 hour |
Cold Crushing Strength | |
| 19.6 - 29.4 MPa @Temperature 1350 °C, Time 10800 sec |
2840 - 4270 psi @Temperature 2460 °F, Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.582 W/m-K @Temperature 260 °C |
4.03 BTU-in/hr-ft²-°F @Temperature 500 °F |
|
| 0.61647 W/m-K @Temperature 540 °C |
4.2714 BTU-in/hr-ft²-°F @Temperature 1000 °F |
||
| Maximum Service Temperature, Air | 1500 °C | 2730 °F | limited |
| Shrinkage | -0.400 % @Temperature 1500 °C, Time 10800 sec |
-0.400 % @Temperature 2730 °F, Time 3.00 hour |
|
| -0.0600 % @Temperature 110 °C, Time 86400 sec |
-0.0600 % @Temperature 230 °F, Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 45 % | 45 % | |
| SiO2 | 47 % | 47 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Casting, Troweling | |
| Material Required for Estimating(kg/?) | 2,100 | |
| Water Required for Casting(%) | 12.0 |
Users viewing this material also viewed the following:
- Akro-Plastic Akromid® B3 S3 75 PA, Dry-Impact Resistant (discontinued **)
- Gouda Vuurvast ADHESIET A Dry Air-Setting Refractory Mortar
- Karina 46/9-G Pearl Color Concentrate for PVC
- A. Schulman PP 2175 Polypropylene High Flow Copolymer Polypropylene
- A. Schulman SUPERLINEAR™ XL 0360 Rotational Molding Resin
- A. Schulman POLYBATCH™ Deep Red 50389 Concentrate Based In Linear Low-Density Polyethylene
- Polymer Resources AC-GP3 Acetal Copolymer, High Flow, Thin Walled Molding (Unverified Data**)
- BASF Neopolen® P 9230 K 0.07 g/cc Core density; Expanded Polypropylene (Europe)
- SABIC Innovative Plastics Geloy FXW710SK ASA/SAN (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved