- Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
- Chi Mei Polylac® PA-764 ABS - Flame Retardant
Chi Mei Polylac® PA-764 ABS - Flame Retardant
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Polylac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Polylac® PA-764 ABS - Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
F.R. Weather Resistant
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 3.3 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.3 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| 33 g/10 min @Load 10.0 kg, Temperature 220 °C |
33 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO-1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 96 | 96 | ASTM D785 |
| Ball Indentation Hardness | 75.0 MPa | 10900 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 29.0 MPa | 4210 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 39.0 MPa | 5660 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 10 % | 10 % | 50 mm/min; ISO 527 |
| Flexural Strength | 55.0 MPa | 7980 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.70 GPa | 247 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 1.22 J/cm @Thickness 6.35 mm |
2.29 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 1.44 J/cm @Thickness 3.17 mm |
2.70 ft-lb/in @Thickness 0.125 in |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180/1C |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | ISO 179 |
| Impact | 9.00 | 9.00 | Impact Flexural Test Notched (KJ/m²) |
| 110 | 110 | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | unannealed; ISO 75 |
| 96.0 °C | 205 °F | annealed; ISO 75 | |
| Vicat Softening Point | 84.0 °C @Load 5.00 kg |
183 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 87.0 °C @Load 5.00 kg |
189 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 98.0 °C @Load 1.00 kg |
208 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| 99.0 °C @Load 1.00 kg |
210 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| Flammability, UL94 | V-0 @Thickness 1.59 mm |
V-0 @Thickness 0.0625 in |
UL 94 |
| 5VA @Thickness 2.54 mm |
5VA @Thickness 0.100 in |
UL 94 |
Users viewing this material also viewed the following:
- Kennametal Stellite Stellite® 712 Cobalt Alloy
- SMAC CABLE® 2518S-60-08 Damping Material
- A. Schulman PP 1247-01 Polypropylene Homopolymer Polypropylene
- Trelleborg AEM Eccospheres® FTD-250 Sodium Borosilicate Glass Microspheres
- Chosun Refractories CTC-60TD Monolithic Refractories for Ladle and Tundish
- Dow TUFLIN™ HSE-1003 NT 7 Linear Low Density Polyethylene Resin
- Bulk Molding Compounds BMC 940 Vinyl Ester Bipolar Plate Material
- ACC EP RP EPI Engineered Polymers Aromatic Polyurea
Copyright © lookpolymers.com All Rights Reserved