Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chi Mei Polylac® PA-746Y ABS  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Medium flow, high impact
Physical Properties Metric English Comments
Density 1.03 g/cc
0.0372 lb/in³
ISO 1183
Melt Flow 15 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 15 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 Melt Volume Rate (ml/10 min); ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 101 MPa
14600 psi
H358/30; ISO 2039-1
Tensile Strength at Break 35.0 MPa
5080 psi
50 mm/min; ISO 527
Tensile Strength, Yield 47.0 MPa
6820 psi
50 mm/min; ISO 527
Elongation at Break 15 %
15 %
50 mm/min; ISO 527
Flexural Strength 65.0 MPa
9430 psi
2 mm/min; ISO 178
Flexural Modulus 2.00 GPa
290 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 23.0 kJ/m²
10.9 ft-lb/in²
ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
ISO 180/1C
Charpy Impact Unnotched NB
NB
ISO 179
Charpy Impact, Notched 2.60 J/cm²
12.4 ft-lb/in²
ISO 179
Impact 17.0
17.0
Impact Flexural Test Notched (KJ/m²)
NB
NB
Impact Flexural Test Unnotched (KJ/m²)
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 86.0 °C
187 °F
unannealed; ISO 75
99.0 °C
210 °F
annealed; ISO 75
Vicat Softening Point 98.0 °C

@Load 5.00 kg
 208 °F

@Load 11.0 lb
 120°C/hr; ISO 306
98.0 °C

@Load 5.00 kg
 208 °F

@Load 11.0 lb
 50°C/hr; ISO 306
104 °C

@Load 1.00 kg
 219 °F

@Load 2.20 lb
 50°C/hr; ISO 306
106 °C

@Load 1.00 kg
 223 °F

@Load 2.20 lb
 120°C/hr; ISO 306
Flammability, UL94 HB

@Thickness 1.59 mm
 HB

@Thickness 0.0625 in
 UL 94