Chi Mei Polylac® PA-707 ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Polylac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Polylac® PA-707 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High gloss, high rigid
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 1.9 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.9 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| 20 g/10 min @Load 10.0 kg, Temperature 220 °C |
20 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO-1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 116 | 116 | ASTM D785 |
| Ball Indentation Hardness | 115 MPa | 16700 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 38.0 MPa | 5510 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 20 % | 20 % | 50 mm/min; ISO 527 |
| Flexural Strength | 79.0 MPa | 11500 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 1.44 J/cm @Thickness 3.17 mm |
2.70 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| 1.44 J/cm @Thickness 6.35 mm |
2.70 ft-lb/in @Thickness 0.250 in |
||
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 90.0 kJ/m² | 42.8 ft-lb/in² | ISO 180/1C |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 1.10 J/cm² | 5.24 ft-lb/in² | ISO 179 |
| Impact | 9.00 | 9.00 | Impact Flexural Test Notched (KJ/m²) |
| NB | NB | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | unannealed; ISO 75 |
| 98.0 °C | 208 °F | annealed; ISO 75 | |
| Vicat Softening Point | 100 °C @Load 5.00 kg |
212 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 102 °C @Load 5.00 kg |
216 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 104 °C @Load 1.00 kg |
219 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 106 °C @Load 1.00 kg |
223 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
UL 94 |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 9002-SR BLK
- Nye Lubricants UniFlor 8921SU (UF) Synthetic Oil
- Polymax® Maxelast® C4960M TPE, Transparent
- Ravago Manufacturing Americas Hylon® N1000HL Nylon 6/6
- Silberline EternaBrite® Premier 251
- TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5) Rod or Thickness, 4.00-6.00 in, Annealed, Per Mil-T-9047G
- Bapolene® PP5021 Polypropylene, Blow Molding Grade
- Axiall 8941 Moldings & Extrusions Flexible PVC
- Overview of materials for Cellulose Acetate Butyrate, Molded
Copyright © lookpolymers.com All Rights Reserved