Chevron Phillips Xtel® XE3200NA Polyphenylene Sulfide Alloy (discontinued **)

Category	Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Chevron Phillips Xtel® XE3200NA Polyphenylene Sulfide Alloy (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Xtel® XE3200NA is an un-reinforced high performance, PPS based alloy developed to provide exceptionally high ductility and impact resistance along with good thermal stability.Information provided by Chevron Phillips

Physical Properties	Metric	English	Comments
Density	1.15 g/cc	0.0415 lb/in³	ISO 1183A
Water Absorption	0.10 %	0.10 %	ASTM D-570

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	30.0 MPa	4350 psi	ISO 527
Elongation at Break	100 %	100 %	ISO 527
Elongation at Yield	10 %	10 %	ISO 527
Modulus of Elasticity	1.20 GPa	174 ksi	ISO 527
Flexural Strength	40.0 MPa	5800 psi	ISO 178
Flexural Modulus	1.10 GPa	160 ksi	ISO 178
Izod Impact, Notched (ISO)	35.0 kJ/m²	16.7 ft-lb/in²	ISO 180A

Thermal Properties	Metric	English	Comments
CTE, linear	150 µm/m-°C @Temperature 20.0 °C	83.3 µin/in-°F @Temperature 68.0 °F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	105 °C	221 °F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	85.0 °C	185 °F	ISO 75

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+14 ohm-cm	1.00e+14 ohm-cm	ASTM D-257
Dielectric Constant	2.8 @Frequency 1e+6 Hz	2.8 @Frequency 1e+6 Hz	ASTM D-150
	2.9 @Frequency 1000 Hz	2.9 @Frequency 1000 Hz	ASTM D-150
Dielectric Strength	24.0 kV/mm	610 kV/in	ASTM D-149
Dissipation Factor	0.0030 @Frequency 1000 Hz	0.0030 @Frequency 1000 Hz	ASTM D-150
	0.0030 @Frequency 1e+6 Hz	0.0030 @Frequency 1e+6 Hz	ASTM D-150
Arc Resistance	95 sec	95 sec	ASTM D-495
Comparative Tracking Index	200 V	200 V	UL 746A

Processing Properties	Metric	English	Comments
Melt Temperature	315 - 345 °C	599 - 653 °F
Mold Temperature	135 °C	275 °F

Users viewing this material also viewed the following: