Material Notes:
Medium density polyethylene. These hexene copolymers are tailored for rotational molding applications that require: Wide process windows and excellent flowLong-term UV stabilizationExcellent impact strengthExcellent ESCR These resins are available in: Pellet form - HMN TR-93535 mesh powder - HMN TR-935GApplications: Recreational and agricultural equipmentToys and cartsInformation provided by PhillipsThese resins meet the following specifications: ASTM D4976 - PE 223FDA 21 CFR 177.1520(c) 3.2a, use conditions B through H per 21 CFR 176.170(c) Table 2. Single use articles contacting food types I, II, IV-B, VI-A, VI-B, VII-B, and VIII. Repeated use articles contacting all food types defined in 21 CFR 176.170(c) Table 1.
Physical Properties Metric English Comments
Density 0.936 g/cc
0.0338 lb/in³
ASTM D-1505
ESCR 100% Igepal® >= 1000 hour
>= 1000 hour
Condition A, F50; ASTM D-1693
ESCR 10% Igepal® 130 hour
130 hour
Condition A, F50; ASTM D-1693
Melt Index of Compound 6.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
6.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D-1238
Mechanical Properties Metric English Comments
Hardness, Shore D 59
59
ASTM D-2240
Tensile Strength, Yield 17.0 MPa
2470 psi
2 in/min, Type IV bar; ASTM D-638
Elongation at Break 750 %
750 %
2 in/min, Type IV bar; ASTM D-638
Flexural Modulus 0.620 GPa
89.9 ksi
2% Secant - 16:1 span:depth, 0.5 in/min; ASTM D-790
0.760 GPa
110 ksi
Tangent - 16:1 span:depth, 0.5 in/min; ASTM D-790
Impact Test 102 J

@Thickness 3.17 mm,
Temperature -40.0 °C
75.2 ft-lb

@Thickness 0.125 in,
Temperature -40.0 °F
ARM Impact
237 J

@Thickness 6.35 mm,
Temperature -40.0 °C
175 ft-lb

@Thickness 0.250 in,
Temperature -40.0 °F
ARM Impact
Thermal Properties Metric English Comments
Melting Point 128 °C
262 °F
ASTM D-3418
Crystallization Temperature 112 °C
234 °F
ASTM D-3418
Deflection Temperature at 0.46 MPa (66 psi) 58.0 °C
136 °F
Method A; ASTM D-648
Deflection Temperature at 1.8 MPa (264 psi) 41.0 °C
106 °F
Method A; ASTM D-648
Vicat Softening Point 110 °C
230 °F
Loading 1, Rate A; ASTM D-1525
Brittleness Temperature -75.0 °C
-103 °F
Type A, Type I specimen; ASTM D-746