Chevron Phillips Marlex® 9506H High Performance Series HDPE Blow Molding Resin (discontinued **)

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Chevron Phillips Marlex® 9506H High Performance Series HDPE Blow Molding Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Resin Type: linear copolymerCharacteristics: superior physical properties, medium molecular weight distribution, wide range of processing conditions, low parison sag, excellent stress crack resistance. Federal specification LP390C Classification Type I, Class H, Grades (1-5), Category 5. Meets FDA Regulation 21CFR 177.1520. Some restrictions apply when containing an antistatic additive.Applications: household and industrial chemicals, industrial blow molding, automotive parts, toys, large trash cans, ice chestsBurn rate < 5 cm/min.Information provided by Chevron Phillips Chemical Company.

Physical Properties	Metric	English	Comments
Density	0.950 g/cc	0.0343 lb/in³	ASTM D1505
Apparent Bulk Density	0.590 g/cc	0.0213 lb/in³	ASTM D1895
Melt Flow	0.27 g/10 min @Load 2.16 kg, Temperature 190 °C	0.27 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	65	65	ASTM D2240
Tensile Strength, Yield	26.9 MPa	3900 psi	ASTM D638
Elongation at Break	>= 500 %	>= 500 %	ASTM D638
Flexural Modulus	1.03 GPa	149 ksi	1% Secant; ASTM D 790
Tensile Impact Strength	115 kJ/m²	54.7 ft-lb/in²	S bar; ASTM D 1822

Thermal Properties	Metric	English	Comments
Vicat Softening Point	124 °C	255 °F	ASTM D1525
Brittleness Temperature	<= -100 °C	<= -148 °F	ASTM D746