Chevron Phillips MarFlex® 9608 HDPE Coating Blend Resin

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer	Chevron Phillips Chemical Company LP
Trade Name	MarFlex®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Chevron Phillips MarFlex® 9608 HDPE Coating Blend Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Resin Type: Coating Blend ResinCharacteristics: Low Gel Levels, Improves MVTR, Reduces COF, Excellent Draw Properties, Excellent Processability, Improves Scuff Resistance, Improves Stiffness PropertiesApplications: Blends, Coextrusions, Food Packaging, Moisture Sensitive Packaging

Physical Properties	Metric	English	Comments
Density	0.962 g/cc	0.0348 lb/in³	ASTM D1505
Melt Flow	8.0 g/10 min	8.0 g/10 min	Cond. E. ASTM D 1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	870 %	870 %	ASTM D882
Film Elongation at Break, TD	790 %	790 %	ASTM D882
Secant Modulus, MD	0.758 GPa	110 ksi	ASTM D882
Secant Modulus, TD	0.841 GPa	122 ksi	ASTM D882
Elmendorf Tear Strength MD	1.4 g	1.4 g	ASTM D1922
Elmendorf Tear Strength, TD	3.90 g/micron	99.1 g/mil	ASTM D1922
Film Tensile Strength at Break, MD	28.9 MPa	4190 psi	ASTM D882
Film Tensile Strength at Break, TD	22.7 MPa	3290 psi	ASTM D882

Optical Properties	Metric	English	Comments
Haze	11 %	11 %	ASTM D1003
Gloss	120 %	120 %	at 60°. ASTM D 2457