Chevron Phillips MarFlex® 9607XD HDPE Cast Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chevron Phillips MarFlex® 9607XD HDPE Cast Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Characteristics: Very Low Gel Levels, Produces Very "Clear" Film, Draws to Thin Gauges, Low Taste and Odor Transfer, Excellent MVTR for a Chill Cast Film, Excellent Processability, Excellent Optical PropertiesApplications:Coextrusions, Overwrap, Food Packaging, Moisture Sensitive PackagingFilm properties below based on film thickness of 31.8 µm.Data provided by Chevron Chemical.
Physical Properties Metric English Comments
Density 0.962 g/cc
0.0348 lb/in³
ASTM D1505
Moisture Vapor Transmission 0.170 cc-mm/m²-24hr-atm
0.432 cc-mil/100 in²-24hr-atm
ASTM F1249
Melt Flow 6.6 g/10 min
6.6 g/10 min
Condition E; ASTM D 1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 870 %
870 %
ASTM D882
Film Elongation at Break, TD 790 %
790 %
ASTM D882
Secant Modulus, MD 0.760 GPa
110 ksi
ASTM D882
Secant Modulus, TD 0.840 GPa
122 ksi
ASTM D882
Elmendorf Tear Strength, MD 1.38 g/micron
35.0 g/mil
Notched; ASTM D1922
Elmendorf Tear Strength, TD 3.94 g/micron
100 g/mil
ASTM D1922
Dart Drop 1.30 g/micron
33.0 g/mil
1.5 in. dart/26 in. drop height; ASTM D 1709
Film Tensile Strength at Break, MD 29.0 MPa
4210 psi
ASTM D882
Film Tensile Strength at Break, TD 23.0 MPa
3340 psi
ASTM D882
Optical Properties Metric English Comments
Haze 11 %
11 %
ASTM D2457
Gloss 120 %
120 %
at 60°. ASTM D 2457